【摘 要】
：
Age hardening in Cu-3.2Ni-0.75Si (wt pct) and Cu-1.0Ni-0.25Si (wt pct) alloys from 723 to 823 K is studied. After an incubation period strengthening appears whi
【机 构】
：
Department of Materials Engineering,Department of Scientific Research
论文部分内容阅读
Age hardening in Cu-3.2Ni-0.75Si (wt pct) and Cu-1.0Ni-0.25Si (wt pct) alloys from 723 to 823 K is studied. After an incubation period strengthening appears which is due to precipitates in the Cu-1.0Ni-0.25Si (wt pct) alloy. On other hand animmediate increase of the yield strength characterizes the aging of the alloy. This is followed by the regions of constant yield strength and further by a peak. The microstructure of the alloy was studied by, means of transmission electron microscope (TEM) and X-ray diffraction (XRD). Spinodal decomposition takes place followed by nucleation of the ordering coherent (Cu,Ni)3Si particles, further precipitation annealing coherent δ-Ni2Si nucleated within the (Cu,Ni)3Si particle. Any change of the yield strength can be described by an adequate change of the structure in the sample. The nature of the aging curves with a"plateau" is discussed. The formulas of Ashby and Labusch can be used to explain the precipitation.
其他文献
To find out the effect of the shape of fused taper region on the optical fiber coupler, the fiber couplers were fabricated at different drawing speeds with a si
The effects of toughener and coupling agent on special epoxy silicone adhesive were discussed by researching the surface morphology characters, thermal properti
The pore structure images of ore particles located at different heights of leaching column were scanned with X-ray computerized tomography (CT) scanner, the por
Microporous titanium dioxide thin films have been grown on titanium plates by the micro-plasma oxidation method with different current densities (4, 6, 10 and 1
The carbonation technique was applied to accelerate the hydration of low heat portland cement (LHC). Before carbonation, the demoulded pastes were precured in w
The combination of ionizing radiation and gene therapy has been investigated. However, there are very few reports about the combination of heavy-ion irradiation
The recent progresses in the surfaee modification of ultra high molecular weight polyethylene (UHMWPE) using such advanced surface modification technologies as
Effect of SiO2 content and sintering process on the composition and properties of Pure CarbonReaction Bonded Silicon Carbide (PCRBSC) ceramics prepared with C -
Au atoms were vaporized by electron beam evaporation, and their subsequent growths on Si (111 ) and highly ordered pyrolytic graphite (HOPG) substrates were stu