Thickness optimization of Mo films for Cu(InGa)Se_2 solar cell applications

来源 :Chinese Physics B | 被引量 : 0次 | 上传用户:mtv138
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
Mo thin films are deposited on soda lime glass (SLG) substrates using DC magnetron sputtering. The Mo film thicknesses are varied from 0.08 μm to 1.5 μm to gain a better understanding of the growth process of the film. The residual stresses and the structural properties of these films are investigated, with attention paid particularly to the film thickness dependence of these properties. Residual stress decreases and yields a typical tensile-to-compressive stress transition with the increase of film thickness at the first stages of film growth. The stress tends to be stable with the further increase of film thickness. Using the Mo film with an optimum thickness of 1 μm as the back contact, the Cu(InGa)Se2 solar cell can reach a conversion efficiency of 13.15%. The thin films are deposited on soda lime glass (SLG) substrates using DC magnetron sputtering. The Mo films thicknesses are varied from 0.08 μm to 1.5 μm to gain a better understanding of the growth process of the film. The residual stresses and the structural properties of these films are investigated, with due thickness of the film thickness dependence of these properties. Using the Mo film with an optimum thickness of 1 μm as the back contact, the Cu (InGa) Se2 solar cell can reach a conversion efficiency of 13.15%.
其他文献
多子是中国传统观念中有福气的象征。在民间,子孙满堂、多子多福是人们最朴素的愿望,但这到了明争暗斗的第一家庭,却往往成了血雨腥风的来源。一切只是因为,皇帝的宝座只有一个,在这些兄弟中,最终只有一个人可以登上权力的巅峰,皇帝的儿子自是再多也不愁养,但愁的是怎么选出这唯一的继承人。为此,兄弟手足之间往往争个你死我活,更有甚者,为早登大位时时期盼乃至下手让亲爹早死。  在历史上,很多皇帝为此甚至不得不防着