【摘 要】
：
AISI302 stainless steel samples were modified by elevated temperature nitrogen plasma immersion ion implantation at temperature ranging from 330 ℃ to 450 ℃. T
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
AISI302 stainless steel samples were modified by elevated temperature nitrogen plasma immersion ion implantation at temperature ranging from 330 ℃ to 450 ℃. The tribological behaviors of the implanted layers of the samples were investigated. The samples were characterized by Auger electron spectroscopy (AES), glancing angle X-ray diffraction (GXRD), and nanoindentation. The results show that the implantation temperature plays an important rule on the microstructure and surface properties of the implanted layers. The thickness of the modified layer implanted at 390 ℃ is about 9 μm. It is improved about two orders compared with that of the implanted at room temperature. The surface nanohardness and the wear resistance of elevated temperature implanted layers increase significantly, and the friction coefficient decreases obviously in comparison with the unimplanted one. These data suggests that the improvement results from the formation of new phases such as ε-(Fe, Cr, Ni)2+xN, or noncrystal phase.
其他文献
A mathematical model to calculate the size and distribution of microporosities was studied and coupled with a stochastic microstructure evolution model. The mod
Mold-filling process of thin-walled castings under the condition of traveling magnetic field has been studied by physical simulation method using gallium melt a
AZ31 Mg alloy was prepared through equal channel angular pressing (ECAP) by Bc route in two different dies, in which the intersecting angles between channels ar
The bond strength of electrodeposited nickel from common electroplate liquid and rare-earth electroplate liquid was tested and contrasted. Electrodeposited nick
The microemulsion AEO-9/butanol/cyclohexane/nitrate aqueous solution (or ammonium salt aqueous solution) was studied, which was used as micro-reactor in prepari
The effect of the deferent rubber content substituted for fine aggregate on the mortar performancewas studied. The effects of the rubber coated with the coating
The nanocrystalline La1-xSrxCrO3 was prepared by sol-gel method using La( NO3 )3 · 6H2O, Sr( NO3 )2 and respectively. The phase transformation from dry-gel to
Electrodeposited Ni matrix/Al microparticles or nanoparticles dispersed composite coatings (termed as EMCCs or ENCCs) are developed from a Ni-based electrolyte
The formation process, microstructure and mechanical properties of transient liquid phase (TLP) bonded aluminium-based metal matrix composite (MMC) joint with c
The reduction diffusion method was performed for the sludge scrap of Nd-Fe-B sintered magnets with adding Ca metal to recover the oxidized Nd-Fe-B phase. After