【摘 要】
：
圆环链经过闪光对焊后弹性模量会发生改变,通过实验测得焊接处不同影响区的弹性模量后针对焊接处进行有限元分析。先在UG中建立圆环链及焊接处的模型,然后导入ANSYS中建立有
论文部分内容阅读
圆环链经过闪光对焊后弹性模量会发生改变,通过实验测得焊接处不同影响区的弹性模量后针对焊接处进行有限元分析。先在UG中建立圆环链及焊接处的模型,然后导入ANSYS中建立有限元模型并计算。最后利用FE-SAFE进行圆环链的疲劳寿命计算,并与实际断裂的圆环链进行比较分析,为以后圆环链的疲劳寿命分析和结构优化设计提供一定依据。
The elastic modulus of the circular chain after flash butt welding will change. The elastic modulus of different affected zone in the weld is measured experimentally, then the finite element analysis is performed on the welding place. First in UG to create a ring chain and welding at the model, and then into the ANSYS finite element model and calculate. Finally, the fatigue life of the circular chain was calculated by FE-SAFE, and compared with the actual broken circular chain, which provided some evidences for the fatigue life analysis and structural optimization design of the circular chain in the future.
其他文献
聚3,4-乙撑二氧噻吩(PEDOT)薄膜的电导率高、稳定性好、透明性佳,有广阔的应用前景。许多科技工作者致力于PEDOT薄膜的制备研究。简要介绍了导电PEDOT薄膜制备方法的研究进展
制备乳酸-氨基酸共聚物是改性聚乳酸的有效方法之一.综述了近年来乳酸-氨基酸共聚物的制备方法与特点,指出了较高分子量和高氨基酸含量聚合物的制备工艺是研发的重点.
采用高温固相法制备了Sr2NaMg2V3O12荧光粉,研究了焙烧温度、保温时间和NH4VO3用量等工艺参数对合成产物发光性能的影响,得出优化的工艺条件为NH4VO3过量1.5％,600℃预烧2h后90
使用ICP-AES同时测定硫酸镍样品中的主量镍和杂质元素钴、铁、铜、锌、钙、镁、镉、铬、锰、铅、钠。方法加标回收率为90%—110%,11次测定的RSD(n=11)小于2.41%,与化工行业标
合成了一种多孔金属有机骨架材料[ZnNa(H3btc)(H2O)2].(H2O)2,分析晶体结构,并采用体积法气体吸附实验,考察了该配合物的吸附气体性能。实验测试结果表是:该配合物为双核,中
为了筛选高放废物深地质处置库中适用的缓冲材料,以内蒙古高庙子天然钙基膨润土和由其改性制备的钠基膨润土为研究对象,分别在120℃、150℃、180℃下热老化3000h、6000h和900
将取代芳基磷酸酯盐类化合物(TMP-5)、多酰胺类化合物(TMC-328)、水滑石(HT)等不同类型的成核剂添加到聚L-乳酸(PLLA)与聚D-乳酸(PDLA)中共混熔融纺丝,初步研究了成核剂对纤
矿用蝴蝶环结构复杂,用传统的经验设计难以得到精确的零件尺寸,通过Creo的零件建模、尺寸关系设定以及有限元分析,可得到精确的设计尺寸,从而缩短设计周期,提高设计精度,节省
通过LS-DYNA对地下爆炸试验模型检测救生舱强度的实验进行模拟,在TNT当量法的基础上用TNT代替瓦斯空气混合气体,得出救生舱壳体在井下瓦斯爆炸时的受力情况;救生舱壳体正面的
为了满足液压支架采高和承载力的增大,大缸径立柱得到了广泛的使用,立柱是液压支架的主要支撑部件,立柱的大小决定了支架的可承载强度和高度;采用厚壁来满足立柱的强度要求。