Nd12.3Fe81.7-xGaxB6.0 (x =0-1.8) ribbons were prepared by melt spinning at 22 m/s and subsequent annealing treatment.The influences of Ga addition and annealing
【机 构】
：
State Key Laboratory for Advanced Metals and Materials,Shandong Jinma Industrial Group Co.
论文部分内容阅读
Nd12.3Fe81.7-xGaxB6.0 (x =0-1.8) ribbons were prepared by melt spinning at 22 m/s and subsequent annealing treatment.The influences of Ga addition and annealing conditions on the magnetic properties and microstructure of the nanocrystalline alloys were systematically investigated.After being annealed at 620℃ for 20 min,the Jr and Hci increased from 0.85 T and 582.6 kA/m for Ga-free sample to 0.97 T and 734.6 kA/m for the x =0.9 sample,respectively.The (BH)max for the x =0.9 sample increased by about 40％ from 96.3 to 135.5 kJ/m3 compared with that of the Ga-free one.The significant improvement of magnetic properties originated from the refmement of grains in the samples by introducing Ga,which led to a stronger exchange coupling between the neighboring grains in comparison with that in Ga-free samples.The microstructure and magnetic properties of the samples depended strongly on annealing parameters,while the sensitivity of microstructure to annealing conditions could be significantly suppressed by the addition of Ga element.
其他文献
In this experiment, strontium borate glasses were prepared using the conventional quenching method in air atmosphere. Optical absorption, photoluminescence exci
In order to investigate the influences of the stoichiometric ratio of B/A (A: gross A-site elements, B: gross B-site elements) and the substitution of Co for Ni
Zirconia-mullite nano-composite ceramics were fabricated by in-situ controlled crystallization of Si-Al-Zr-O amorphous bulk, which were first treated at 900-1 0
Micro/nanostructured crystals with controlled architectures are desirable for many applications in optics, electronics, biology, medicine, and energy conversion
全球金融危机后，国际社会从一个新的视角---影子银行体系来分析现代金融体系，并重构现代国际金融监管制度。影子银行体系的有效监管必须具有翔实的微观基础，比如明确体系边界、
The nanocrystalline β-SiC powder was successfully synthesized by ball milling the Si-50%C elemental powder. During ball milling, a solid solution of C in Si, S
In this article, we report the results of our detailed investigations of the growth kinetics of zero-dimensional nanocrystals as well as one-dimensional nanorod
Al-Ti-C-Y master alloy was prepared by combining SHS technique and melting-casting method. The microstructure of master alloy and its grain-refining effect on A
The substrate pre-treatment plays a key role in obtaining hollow-cored carbon nanotubes (CNTs) and solidcored carbon nanofibers (CNFs) from flames. This paper i
Single fiber pull-out testing was conducted to study the origin of the functional responses to loading of carbon fiber reinforced cement-based composites.The va