Anodization of AZ91D magnesium alloy in the electrolyte solution of 0.5 mol/L of sodium silicate and 1.0 mol/L of potassium fluoride was investigated. The anodic films were characterized using optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffraction (XRD). The corrosion resistance of the various anodized alloys was evaluated by a fast corrosion test using the solution of hydrochloric acid and potassium dichromate. The results showed that the addition of KF resulted in the presence of NaF in the anodic film. The thickness of the anodic film formed under a constant current density of 20 mA/cm2 for 16 min at 60℃ exceeded 100 μm. The growth of the anodic film could be divided into three stages based on the anodizing time; the growth rate was much faster during stage Ⅱ than in stages Ⅰ and Ⅲ. The anodic film exhibited the highest corrosion resistance for the AZ91 alloy,which is attributed to the fact that the anodization was maintained until the end of stage Ⅱ.