The 8％ (mass fraction) yttrium-partially-stabilized zirconia (8YSZ) ceramic was fabricated via liquid phase sintering at 1 200-1 400 ℃ by adding different mass
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
The 8％ (mass fraction) yttrium-partially-stabilized zirconia (8YSZ) ceramic was fabricated via liquid phase sintering at 1 200-1 400 ℃ by adding different mass ratios of CuO-16.7％TiO2 (molar fraction) as sintering aid.Relative density,microstructure,Vickers hardness and bending strength as a function of sintering temperature and additive content were investigated.The experiment results show that liquid phase sintering at low temperature can be realized through adding CuO-16.7％ TiO2 to 8YSZ.The Vickers hardness and bending strength of samples with sintering aid are generally much higher than those of samples without sintering aid for all sintering temperatures,and increase with the increase of sintering temperature.When the addition content of CuO-16.7％ TiO2 is beyond 0.5％,the relative density,Vickers hardness and bending strength decrease with the increase of the mass ratio of sintering aid.Low additions of sintering aid are beneficial to aiding densification; high additions of sintering aid are detrimental to the sintered properties mainly due to greater amounts of pores generated by the volatilization of oxygen with the eutectic reaction between copper oxide and titanium dioxide.It is found that the fine grain size and high relative density are two main reasons of the high bending strength and Vickers hardness of the materials.
其他文献
Achieving simultaneous reduction of NOx,CO and unburned hydrocarbon (UHC) emissions without compromising engine performance at part loads is the current focus o
In magnetic Czochralski (MCZ) silicon growth,the distance and diameter of the electrified coils may affect the magnetic field intensity and melt flow.By changin
Optical microscopy (OM) and transmission electron microscopy (TEM) were used to investigate the effect of tempering temperature on the experimental extra-high c
This paper demonstrated our discovery of the movement effect of BiFeO3 nanoparticles in solution by strong electrical polarization.First,BiFeO3 nanoparticles we
Aging precipitation and solid solution heat treatment were carried out on three steels which have chromium content of 18％,manganese content of 12％,15％,18％,and nitro
Abstract:Spinel compounds LiNi0.5Mn1.3Ti0.2O4 (LNMTO) and Li4Ti5O12 (LTO) were synthesized by different methods.The particle sizes of LNMTO and LTO are 0.5-2 an
Auger electron spectroscopy (AES) was used to investigate the grain boundary segregation of arsenic and nitrogen in a kind of microalloyed steel produced by a c
In order to meet the severe requirements of market and reduce production costs of high quality steels,advanced run-out table cooling based on ultra fast cooling
A novel photocatalyst,bismuth oxychloride (BiOCI) micro-nano particles with a fine ferrite plate structure,was prepared by a low-cost,simple hydrolytic method.T