论文部分内容阅读
This paper deals with structure and impact energy of weld HAZ of 10CrNi3MoV steel after secondary weld thermal cycle (t8/5=8(¨)s~120(¨)s; peak temperature Tm=750℃~1(¨)300℃). It is demonstrated that the coarse grain and structure produced by first thermal cycle keep unchanged after secondary thermal cycle above Ac1 critical temperature but below 1(¨)050(¨)℃. At the same time the low temperature impact energy decreases obviously with increasing t8/5. By metallurgical microscope and transmission electron microscope(TEM) , it is revealed that the effect of coarse grain and structure caused by secondary thermal cycle on low temperature impact energy.