【摘 要】
：
报道了单辊法制备的三个系列11种CuPNISn非晶合金的晶化温度、熔化温度区间、流布面积、Cu-Cu对接接头的抗拉强度及钎缝显微组织的分析结果。发现铈的加入可明显提高钎焊接头
【机 构】
：
湖南大学应用物理系,湖南大学应用物理系,湖南大学应用物理系 长沙 410012,长沙 410012,长沙 410012
论文部分内容阅读
报道了单辊法制备的三个系列11种CuPNISn非晶合金的晶化温度、熔化温度区间、流布面积、Cu-Cu对接接头的抗拉强度及钎缝显微组织的分析结果。发现铈的加入可明显提高钎焊接头强度,并细化晶粒。同时还发现随焊料中(Ni+Sn)含量的降低,接头从脆性断裂变为韧性断裂,其抗拉强度大大高于母材的屈服强度。
The crystallization temperature, the melting temperature interval, the flow area, the tensile strength of Cu-Cu butt joint and the analysis results of the brazing seam microstructure of eleven series of 11 CuPNISn amorphous alloys prepared by single-roll method are reported. Found that the addition of cerium can significantly improve the strength of the brazed joints, and grain refinement. At the same time, it is also found that with the decrease of (Ni + Sn) content in the solder, the joint changes from brittle fracture to ductile fracture, and its tensile strength is much higher than the yield strength of the base metal.
其他文献
据英国《化学专利文摘》周刊1992年第28期报道,一种具有高矫顽磁力和高剩余磁通密度的稀土永磁材料于1992年5月28日在日本获得专利,专利号为JP04155902A。 永磁材料的主要成
残阳如血,我坐在窗前,用力点上最后一个点,以一个大大的感叹号当作最后的结尾。随笔本上墨迹未干,似乎依旧有什么等待我去完成。夕阳西下,黄昏的余光在天际聚拢、迸发。那一
我是出了名的书虫,在学校里最喜欢的地方,大概就是图书馆里放着文学小说的那两排大书架了。一入学就发下宏愿,要在毕业之前将这两个大书架上满满当当的中外小说全部读上一遍,
一我以前一直认为,像郑莱莱这样四体不勤五谷不分的公主型女生,大概最擅长的就是尖叫和眼泪汪汪了吧?半个学期了,我才发现郑莱莱还有一个爱好,或者说习惯——坚持写日记。“
用透射电子显微术和X射线能谱术研究了Ti_3Al-11Nb(Ti-12.5wt%Al-21wt%Nb)合金热锻棒材在热处理过程中的相变特征。结果表明,合金在1100℃加热后缓冷到室温的样品其组织由α_
近年来有机非线性光学及其材料的研究受到极大关注。其中具有代表性的是带有非线性基团的硝基苯胺衍生物,它们的分子不具有对称中心,含有TT共轭电子体系並具有分子内发生电
日本原子能研究所高温工程部简介日本原子能研究所(JAERI)计划建造一个高温气体冷却反应堆(HTGR),这种高温工程试验堆(HTTR)的设计是用石墨作为减速剂,氦气冷却,热输出30MW,
继去年9月和Fossil合作推出蓝牙手表MBW-100之后,索尼爱立信和Fossil近日又合作推出了新系列蓝牙手表MBW-150,包括音乐(Music)、经典(Classic)和尊贵(Executive)三个版本。
捕捉你心灵深处的故事吧,感动了你的也将感动我们。留言编者每个人都走在自己的路上,并排时的相望,交错时的会意,你的心中可曾留住对方的气息,并在别人眼里种下一段缘分?生活
介绍利用高频电磁感应加热重熔NiWC25金属合金粉末涂层与基体结合机理的有关研究结果。采用电子扫描显微镜、波谱分析及能谱分析等手段,证明了涂层与基体具有明显的钎焊特征;