【摘 要】
：
采用放电等离子烧结(SPS)设备制备了W-Re高比重合金,烧结温度为1800℃,烧结压力为40MPa,保温时间为5min。对SPS烧结的W-Re合金试样进行了密度、硬度等性能测试。采用金相显微
【机 构】
：
昆明贵金属研究所稀贵金属综合利用新技术国家重点实验室,
论文部分内容阅读
采用放电等离子烧结(SPS)设备制备了W-Re高比重合金,烧结温度为1800℃,烧结压力为40MPa,保温时间为5min。对SPS烧结的W-Re合金试样进行了密度、硬度等性能测试。采用金相显微镜观察试样的金相组织、晶粒大小。结果表明:采用SPS烧结,可以在较低的温度下实现W-Re合金的致密化,并能有效控制晶粒长大,提高材料的硬度。
W-Re alloy with high specific gravity was prepared by spark plasma sintering (SPS). The sintering temperature was 1800 ℃, the sintering pressure was 40MPa and the holding time was 5min. The SPS sintered W-Re alloy samples were tested for their density, hardness and other properties. Metallographic microscope was used to observe the microstructure and grain size of the sample. The results show that using SPS sintering, the W-Re alloy can be densified at lower temperature and the grain growth can be effectively controlled and the hardness of the W-Re alloy can be increased.
其他文献
本刊讯(记者 乔思伟)今年全国两会上,全国政协常委、人口资源环境委员会副主任姜大明,全国政协常委、民盟中央副主席曹卫星,全国政协委员王世元、张德霖、严之尧,联名提案建
用软盘拷贝传递文件是日常利用计算机办公系统经常需要做的工作.但是在实际工作中可能常会遇到这样的问题:需要拷贝的文件往往超过了一张软盘的容量,而一时又找不到合适的压
【摘 要】水是农业经济的命脉，随着世界性淡水资源日趋短缺，水资源供需矛盾的日益加剧，水已成为制约经济社会可持续发展的主要瓶颈。本文围绕吐鲁番市节水工作存在的问题和原因，提出节水工作的后续发展方向，达到合理利用水资源的目标。 【关键词】节水工作；用水状况；存在问题；发展方向 节水型社会建设，是指一种和谐社会形态，即指水资源集约高效利用、经济持续快速发展、人与自然和谐相处的社会。水是农业经济的命脉
2011年11月7日，美国著名品牌NINE WEST2012春夏新品全球媒体巡展抵达上海。NINEWEST创意总监Fred Allard先生亲临外滩，在水舍与国内顶尖的时尚业界人士一同领略NINE WEST 2012
新一届政府提出的新城镇化路线,中国现有的金融体系必然要为其匹配一套有效地融资渠道和融资工具。回顾过往中国地方政府的融资实践,由于受到法律法规限制,平台贷款、债券融
本论文分别以黄酮、香豆素作为发光基团,设计、合成了识别氟离子(F-)和生物巯基化合物(还原性谷胱甘肽和半胱氨酸)的光化学传感器,并研究其光谱性质和识别机制,另外我们在硅
<正>夏季来临,向大家推荐一款养生汤——冬瓜太金汤。这道汤兼具保健、养颜、瘦身、清暑、益气之功效,制作简单,取材方便,堪称入夏养生第一汤。用料与制法:冬瓜400克,咸肉或
本文介绍了日本近年来在生态设计方面开展的一些研究项目和取得的成果,还以日立公司为例,介绍了日本企业在生态设计方面先进的理念和实施经验,为我国电器企业实施产品生态设