SrAl2 O4: Eu, Dy nanometer phosphors were synthesized by combustion method at 500 ～ 900℃, followed by heating the combustion sample at 1150℃ at a weak reductive atmosphere and nanometer phosphor with much better luminescent properties was obtained. The influences of the initiating combustion temperature, H3BO3 quantity, the mass ratio of urea and nitrate on the luminescent intensity of nanometer phosphors were studied. The optimum synthetic conditions were determined. The analysis results by transmission electron microscopy (TEM) indicate that the particle size of the synthetic product is less than 75 nm. The luminescent materials do not need to be ground. Their coating can be refined. It supplies a new approach to the rapid preparation of the luminescent materials at low temperature. The excitation and emission spectra indicate that the main peaks in the excitation and emission spectrum of nanometer phosphor synthesized by combustion method shifted to the short wavelength compared with the phosphor obtained by the solidstate reaction synthesis method. The reason of blue shift was explained. The afterglow decay results indicate that the decay speed of the afterglow for nanometer phosphor is faster than that obtained by the solid-state reaction method.