In the process of high-k films fabrication, a novel multi deposition multi annealing(MDMA) technique is introduced to replace simple post deposition annealing. The leakage current decreases with the increase of the post deposition annealing(PDA) times. The equivalent oxide thickness(EOT) decreases when the annealing time(s) change from 1 to 2. Furthermore,the characteristics of SILC(stress-induced leakage current) for an ultra-thin SiO_2/HfO_2 gate dielectric stack are studied systematically. The increase of the PDA time(s) from 1 to 2 can decrease the defect and defect generation rate in the HK layer. However, increasing the PDA times to 4 and 7 may introduce too much oxygen, therefore the type of oxygen vacancy changes.
The process of high-k film fabrication, a novel multi deposition multi annealing (MDMA) technique is introduced to replace simple post deposition annealing. The leakage current decreases with the increase of the post deposition annealing (PDA) times. The equivalent oxide thickness (EOT) decreases when the annealing time (s) change from 1 to 2. Furthermore, the characteristics of SILC (stress-induced leakage current) for an ultra-thin SiO 2 / HfO 2 gate dielectric stack are studied systematically. However, increasing the PDA times to 4 and 7 may introduce too much oxygen, therefore the type of oxygen vacancy changes.