The characteristics of 5A90 Aluminum-Lithium alloy by YAG laser and MIG arc hybrid welding (Hybrid welding) were studied.Compared with the laser beam welding (LBW),the hybrid welding could not only improve the weld appearance significantly,but also have better engineering compatibility.The obvious microstructure characteristics of joint by the hybrid welding are fine-grained layer near fusion-line and the equiaxed grain in most area of welded seam.The subgrains of the equiaxed grains,located in the weld center,tend to coarse from bottom to top of weld joint.The microhardness of welded seam by the hybrid welding (83.57HV0.2) is lower than that by LBW (95.65HV0.2),but the uniformity of the former is better than that of the latter.The ultimate strength and the elongations after fracture of the joint by the hybrid welding are lower than that by LBW.The tensile fracture always occurs in HAZ or weld centerline,and the fractography presents mixture rupture.Therefore,if the combined mechanical properties of joint by the hybrid welding meet the operation requirements,it should be improved by reasonable artificial aging or heat treatment after welding,and it also should develop a better filler wire matched with the base metal. The characteristics of 5A90 Aluminum-Lithium alloy by YAG laser and MIG arc hybrid welding (Hybrid welding) were studied. Compared with the laser beam welding (LBW), the hybrid welding could not only improve the weld apparent significantly, but also have better engineering compatibility.The obvious microstructure characteristics of joint by the hybrid welding are fine-grained layer near fusion-line and the equiaxed grain in most area of ​​welded seam. subgrains of the equiaxed grains, located in the weld center, tend to coarse from bottom to top of weld joint. The microhardness of welded seam by the hybrid welding (83.57HV0.2) is lower than that by LBW (95.65HV0.2), but the uniformity of the former is better than that of the latter. ultimate strength and the elongations after fracture of the joint by the hybrid welding are lower than that by LBW. The tensile fracture always occurs in HAZ or weld centerline, and the fractography presents mixture rupture.Therefore, if the combined mechanical properties of joint by the hybrid welding meet the operation requirements, it should be improved by reasonable artificial aging or heat treatment after welding, and it also should develop a filler wire matched with the base metal.