【摘 要】
：
采用等离子熔覆技术在42CrMo表面制备耐磨合金层,通过金相显微镜、X射线衍射仪对熔覆层显微组织及物相进行观察分析,采用维氏硬度仪测量熔覆层金属的显微硬度,选用磨损试验机
【机 构】
：
郑煤集团(河南)白坪煤业有限公司,河南省煤科院耐磨技术有限公司,河南省新郑煤电有限责任公司,
论文部分内容阅读
采用等离子熔覆技术在42CrMo表面制备耐磨合金层,通过金相显微镜、X射线衍射仪对熔覆层显微组织及物相进行观察分析,采用维氏硬度仪测量熔覆层金属的显微硬度,选用磨损试验机对熔覆层金属耐磨性能进行检测。结果表明:与等离子熔覆制备1Cr13合金层相比,通过等离子熔覆-注入技术制备1Cr13-B4C复合合金层,其熔覆层显微组织晶粒细化,硬度与耐磨性能显著提高。
The wear-resistant alloy layer was prepared on the surface of 42CrMo by plasma cladding technique. The microstructure and phase of cladding layer were observed and analyzed by metallographic microscope and X-ray diffractometer. The microstructure of cladding layer was measured by Vickers hardness tester Hardness, the choice of wear testing machine cladding metal wear resistance testing. The results show that the microstructure of 1Cr13-B4C composite alloy prepared by plasma cladding-injection technique is more refined and the hardness and abrasion resistance are significantly improved than that of 1Cr13 alloy prepared by plasma cladding.
其他文献
为了改善ZN-1材料与硬铝的粘接性能,在采用环氧胶黏剂情况下,通过不同方式对橡胶材料表面进行了处理。研究表明,采用打磨、清洗橡胶表面的方式对提高粘接强度并无帮助,而采用
制得一种复合膜修饰玻碳电极HPMαFP/Ppy/GCE（HPMαFP：1-苯基-3-甲基-4-（α-呋喃甲酰基）-5-吡唑啉酮，/Ppy：聚吡咯, GCE：玻碳电极）。通过循环伏安法（CV）和脉冲伏安法（DPV）研究了氧氟沙星（OF
研究了三维激光扫描测头的数学模型,构建一种面向现场的三坐标视觉测量系统。其标定方法基于平面自由移动靶标,设计了基于二次曲面拟合的空间几何参数测量方法。实验结果表明在测量范围为900mm×600mm×600mm的情况下,测量误差范围小于0.3%。
目的：为了筛选出适合用于组织工程皮肤的膜支架材料，采用不同来源的纤维素（木、棉、竹），与壳聚糖以及海藻酸钠等多糖为原料制备了多种复合膜，并表征了其理化性能。方法分别配制木、
平面激光诱导荧光（ PLTF）用于测量流体流动过程的浓度场，混合流体的浓度和温度及示踪物质的浓度都会对结果产生影响。为了把PLTF方法用于黏性流体的混合研究，设计实验用以探究混
基于开源程序OpenFOAM和动网格技术，利用切应力平衡法建立水流作用下的海上风电基础局部冲刷数学模型。通过模拟结果与实验数据的对比发现，所建立的冲刷数学模型能够合理反映圆
癫痫是临床常见的慢性发作性疾病,因其发作的复杂性和多样性,对致痫灶的定位及癫痫网络的研究一直成为热点.静息态功能磁共振成像(rs-fMRI)可研究大脑静息状态下自发活动,已
本文针对豫西“三软”煤层特点，设计一种新型拉杆式炮采、机采两用液压支架，介绍该拉杆液压支架主要技术参数，分析了主要部件结构及特点以及对通过现场专家会审对支架进行的几处
制备了具有酸性功能的离子液体[Hnmp] HSO4,并用其催化菜籽油酯交换制备生物柴油.该离子液体表现出良好的催化活性及稳定性.在醇油比为8∶1、反应温度(100±2)℃、反应时间5h
采用交联剂戊二醛将漆酶固载在Fe3O4/SiO2纳米粒子上,用于偶氮荧光桃红的脱色降解研究.试验结果表明,固定化漆酶对10～70mg· L-1偶氮荧光桃红脱色率均可达到90％以上,降解率可达