The feasibility of reducing Cr(VI) from the aqueous solution by sulfuric acid-modified titanium-bearing blast furnace slag (SATBBFS) as a photocatalyst was inve
【机 构】
：
Department of Materials Science and Engineering,School of Materials and Metallurgy
论文部分内容阅读
The feasibility of reducing Cr(VI) from the aqueous solution by sulfuric acid-modified titanium-bearing blast furnace slag (SATBBFS) as a photocatalyst was investigated. The photocatalysts were examined by X-ray diffraction (XRD), UV-vis diffuse reflectance spectra, thermogravimetric analysis (TG) and Fourier transform infrared spectroscopy (FTIR). The photocatalytic activities of the different catalysts were evaluated by the photocatalytic reduction of Cr(VI) under UV-vis light irradiation. The results show that the photocatalytic activities of SATBBFS catalysts are strongly dependent on CaTiO3-to-TiO2 mass ratio, adsorption capacity and surface acidity, and SATBBFS calcined at 400 ℃ shows a higher photocatalytic activity compared with other catalysts.
其他文献
由于生态基流需求不是完全由单个机构决定,而是多个水管理团体共同决策的结果,这就对水管理的领导力提出了挑战。当单纯依靠技术方法不能解决问题时,就需要依靠领导力来应对
尽管低水头坝规模小,但可能会对水上娱乐人群的人身安全构成威胁。最近在美国某水坝中发生的溺水事件受到了广泛关注,因此水坝管理者与公众双方都必须增强安全意识。从低水头
介绍了玻璃钢的主要性能和玻璃钢作为新材料在铁路客车内装上的应用前景。
Introduced the main performance of FRP and FRP as a new material installed in the railway
介绍低汞节能灯生产中的工艺控制要点,对比汞减量技术实施前后的试验数据,说明适当的低汞工艺可在确保灯参数达标的同时,有效减少用汞量.
理论分析了相控阵超声检测技术特点,通过设计一种专用相控阵超声检测换能器,控制换能器各阵元的聚焦、扫查,将获得的数据进行软件分析,从而实现菌型叶根二维成像检测。该检测
本文针对9FB型余热锅炉入口烟道内部高温度、高流速的特性,开发设计了新型的导流结构.在使烟气均匀分布的同时,避免高流速烟气对受热面的破坏.
主要论述贮氢合金理论模型研究进展.内容主要涉及贮氢合金的电子结构与氢化物稳定性之间的关系,合金材料的热力学研究,合金电极反应等方面.充分有效利用贮氢合金理论模型,将
人与自然的关系历来是文学创作永恒的主题.人类的生存与发展过程实质上就是人与自然矛盾不断展开和不断解决的循环过程.马克思曾说过:“社会是人同自然界完成了本质的统一,才
Mg粉在800℃氨气流中氨化60 min,可得到高质量的Mg3N2粉末.XRD分析表明,Mg3N2粉末是体心立方结构,晶格常数a=0.996 57 nm.SEM分析表明,Mg3N2粉末有多种形貌.PL测试表明,在激
采用"阶梯"铸件,设计了压铸过程模具温度测量的实验方案并进行了压铸实验.以实验中测得的铸型内部不同位置的温度为基础,采用热传导反算法求解了压铸过程中铸件/铸型界面热流