锻造流线取向对超高强钢抗腐蚀性能的影响

来源 :热加工工艺 | 被引量 : 0次 | 上传用户:ellen
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
采用慢应变速率拉伸试验和动电位极化研究了锻造流线方向对23Co13Ni11Cr3Mo超高强钢在3.5%NaCl溶液中的腐蚀性能的影响。结果表明,通过慢应变速率拉伸试验(SSRT),应力腐蚀开裂敏感性随锻造流线与腐蚀面的角度增大而增大,而腐蚀电位降低,腐蚀电流密度增大。沿锻造流线取向的抗腐蚀性能最好,垂直于锻造流线取向的抗腐蚀性最差。 The effects of forging flow direction on the corrosion behavior of 23Co13Ni11Cr3Mo ultra-high strength steel in 3.5% NaCl solution were investigated by slow strain rate tensile test and potentiodynamic polarization. The results show that the susceptibility to stress corrosion cracking increases with the increase of the angle of forging flow lines and corrosion surface through the slow strain rate tensile test (SSRT), while the corrosion potential decreases and the corrosion current density increases. Corrosion resistance along the forging streamline orientation is best, and corrosion resistance perpendicular to the forging streamline orientation is the worst.
其他文献
建设民航强国是中国民航人多年的梦想。2010年,民航局局长李家祥以一席《中国民航人要为建设民航强国而努力奋斗》的讲话开启了全行业全面实施民航强国战略的大门。中国民航
自2009年3月25日国务院常务会议审议并原则通过《关于推进上海加快发展现代服务业和先进制造业,建设国际金融中心和国际航运中心的意见》正式批准实施上海“双中心”建设规划以来,上海的“双中心”建设不断向前推进。  1 现代航运业与金融业的关系  现代航运业与金融业密不可分、相辅相成、相互促进,航运金融业也因此发展起来。航运金融业目前的业务主要有两个方面,一是船舶融资,二是航运保险。航运企业通过融资扩
近年来,我国建筑行业模板脚手架支撑体系在施工过程中多次发生坍塌事故,造成重大人员伤亡和财产损失。此类安全事故的发生,原因是多方面的,但其中模板、脚手 In recent year
采用大涡模拟(LES)方法对有/无等离子体激励条件下不同射流角时的平板气膜冷却流场进行了对比研究。结果表明:随着射流角的增大,冷却射流对主流的穿透率与气膜孔下游回流区的
《ATW》2011年2月版刊登Katie Cantle在北京写的分析文章,谈中国航空公司未来五年黄金时期,文章题目:AGolden Opportunity.中文大意:黄金机遇。业界广泛认为,未来五年中国的
本刊讯4月7日,中国民用航空局副局长王昌顺在贵阳召开的全国民航规划暨机场工作会议上宣布,《中国民用航空发展第十二个五年规划》(以下简称《规划》)正式出台。根据《规划》
2011年1月19日,全省安全生产监管暨反腐倡廉工作会在长春召开。会议认真学习贯彻了全国安全生产工作会议和王儒林省长,王祖继副省长的重要讲话精神,回顾了2010年和“十一五”
在工程施工、线路检修中,作业人员在蹬杆时,特别是在阴雨、霜冻、下雪等天气后,由于电杆表面有水露或霜冻,很容易发生脚扣打滑,加之所使用的安全带没有防高空滑落的功能,作业
烟花爆竹是给人们带来欢乐和吉祥的产品,面对近几年春节期间连续发生因普通消费者个人燃放烟花爆竹不当引发人员伤亡和财产损失的安全事故,我们烟花爆竹行业协会和广大企业深
将冲击冷却技术与肋化表面相结合,研究了一种具有微小W型肋的表面射流冲击冷却结构。通过稳态实验和瞬态热色液晶测试技术来探究光滑靶板和微小W型肋靶板的传热特性。测试时