SAPO-34,SAPO-5/34 based catalysts doped with Cu,Ce as active components were synthesized via a one-pot hydrothermal method by using different amounts of additiv
【机 构】
：
College of Chemistry and Chemical Engineering,Qiqihar University,Qiqihar 161006,China;College of Mat
论文部分内容阅读
SAPO-34,SAPO-5/34 based catalysts doped with Cu,Ce as active components were synthesized via a one-pot hydrothermal method by using different amounts of additive (α-cellulose),and their catalytic activities were measured for selective catalytic reduction (SCR) of NO with NH3.The synthesized Cu-Ce co-doped products switch from cubic SAPO-34,to flower-like aggregated SAPO-5/34,hybrid crystal SAPO-5/34,and finally to spherical aggregated SAPO-34 with the increase of α-cellulose amount.The Cu-Ce co-doped SAPO-5/34 hybrid crystal structure catalysts with 0.75 mol ratios of C/P (Cu-Ce/SP-0.75)exhibit excellent NH3-SCR activity with higher than 90％ NOx conversion in the temperature range of 180-450 ℃,at WHSV of 20000 mL/(g· h).Furthermore,the catalyst displays outstanding sulfur resistance and NOx conversion maintains above 90％ at 200-450 ℃ after adding 100 ppm of SO2.The characteristic results suggest that the high deNOx performance of Cu-Ce/SP-0.75 is due to the enhanced accessibility,abundant activity species,excellent redox property and high adsorptive and activated capacity for NH3.
其他文献
农作物品质与立地环境地球化学条件关系密切,探明种植区岩石-土壤-植株系统的元素地球化学特征对作物生产具有重要意义.采用野外实地调查与室内分析相结合的方法对贵州蓝莓核
离子吸附型稀土矿床的稀土配分是决定矿床价值的重要因素,以ΣYO,Eu2O3,Y2O3作为划分依据评价矿床经济价值目前已不合理。本文通过收集近3年稀土产品价格和40个离子吸附型稀土矿山配分数据,分析40个不同稀土配分的矿山价值,并进行对比研究,提出了以ΣYO,Pr6O11+Nd2O3和Tb4O7+Dy2O3为划分依据的稀土配分类型分类
红外滤光片,尤其是中长波红外窄带滤光片等光谱指标要求较高的红外光学薄膜,膜层厚度能达到几十微米,因而对膜料的需求非常大。当镀膜真空室较大时,一次填料不能满足膜料用量需求,通常采用减小蒸发距离的方式提高膜料的利用率,但同时会使膜厚均匀性变差,光谱性能变差。通过镀膜理论分析,在满足产品镀膜均匀性的前提下,设计了一套可自由调节高度及大小的旋转平面基片工装,以减小蒸发源与镀膜基片的距离,提高膜料利用率。理论计算表明,当工件盘和蒸发源之间的垂直高度与蒸发源和工件盘转轴的距离之比为1.8、蒸发源是小平面源时,膜厚不均
We investigated the magnetocaloric effect in commercial Er2O3 powders which presents almost no hysteresis losses at low temperature.At a magnetic field change o
为了探究用复合技术制备的DLC复合薄膜的力学性能和耐腐蚀性能,采用多弧离子镀(MAIP)和非平衡磁控溅射技术(UBMS)分别在316L不锈钢基底上沉积了H-DLC、TiN和TiN/H-DLC薄膜。采用三维轮廓仪、扫描电镜以及拉曼光谱分析薄膜的形貌和微观结构,采用纳米压痕仪、划痕仪、CSM摩擦试验机和电化学工作站表征了薄膜的纳米硬度、膜基结合力、摩擦学性能和耐腐蚀性能。结果表明,用多弧离子镀引入TiN层能够有效提高TiN/H-DLC复合薄膜的结合力并降低摩擦因数,但是薄膜的磨损率未明显降低,其原因可能是表面
本文将电场诱导与热化学气相沉积(CVD)直接生长技术相结合,在合金基底上得到了垂直排列的多壁碳纳米管(MWNT)薄膜,MWNT直径约50 nm、长度约2~3μm。施加电场生长的MWNT的晶体性优于未加电场生长的MWNT,它们的拉曼光谱中D峰与G峰强度比值ID/IG平均值分别为0.76和0.87。垂直排列的MWNT与随机排列的MWNT的开启电场分别为3.0 V/μm和3.8 V/μm;在相同的测试电场下,前者有更高的场发射电流密度,低电流发射稳定性良好,但是MWNT相对密集,电场屏蔽效应较强。采取措施进一步
简略介绍相对论和量子力学的基本原理,引用最新的新闻报导,论述真空科学技术在相对论和量子力学研究中的应用和最新进展.众所周知(包括没写入书本的内容)如:真空是宇宙之母,
原子频标是典型的量子电子学产物,它可以输出稳定的频率信号,在导航、守时、授时以及通信等国计民生的各个方面都有重要的作用。原子频标制造过程中采用薄膜技术可以有效地提高原子频标的性能和使用寿命。本文首先阐述了传统铷、铯、氢原子频标中薄膜技术的应用,即薄膜技术在铷原子频标中用于光谱灯优化和光频移抑制,以改善铷原子频标的稳定度和漂移;在铯原子频标中用于电子倍增器研制及其新工艺和新方法的研究,用以提高铯束管的寿命和信噪比;在氢原子频标中用于氢原子存储,降低氢原子与泡壁的碰撞概率,延长氢原子弛豫时间,提升信噪比。其次
利用γ射线源,开展了空间用轻火石(QF)玻璃的空间辐射效应及试验方法研究。研究了QF在不同总剂量辐照条件下的性能退化规律。获得了轻火石玻璃最大辐照剂量达100 Mrad的辐射效应试验数据,总结了QF玻璃辐射效应变化规律。通过光谱解析等方法,分析了QF玻璃空间辐射效应机理及辐射损伤来源。建立了QF玻璃性能退化模型,QF玻璃随辐照剂量的增大呈现指数衰减规律。进行了QF玻璃在常温、343 K及373 K条件下的退火试验,总结了QF玻璃的退火规律,并将退火的影响应用于控制光学玻璃材料辐照后测试时间。
低温,尤其是低于24.5561 K(氖三相点)温区,常用的三种标准电阻温度计是铂、铑铁和铂钴电阻温度计。铂钴电阻温度计在20 K以下的灵敏度和稳定性与铑铁电阻温度计相近,可作为精密测温的标准器使用,越来越受到低温界的重视。本文研究了自研的铂金壳标准铂钴电阻温度计低温温循后的短期稳定性,介绍了标准铂钴电阻温度计低温温循考核流程、水三相点标定装置和用于温度计液氮温循的装置,完成了4支标准铂钴电阻温度计在室温至液氮温区的温循考核测试。经过20次温循后,水三相点的稳定性测试结果显示,最优的铂钴温度计稳定性为0.3