【摘 要】大多数工程使用胶粉聚苯颗粒保温砂浆作为建筑外墙的外保温，有的在保温材料上粘贴面砖，防止面砖开裂、空鼓，本文对胶粉聚苯颗粒保温砂浆上粘贴面砖进行探讨。
【关键词】保温砂浆；外墙外保温系统；面砖
The gum powder gatherbenzene grain heat preservation sand wall outsidesyrupstick noodles brick analysis
Xiao Jian-ming,Xi Jun-feng
(taixin city zhongxin construction engineering quality examination center limited company Taixin Jiangsu 225400)
【Abstract】Majority engineering usage gum powder's gather the benzene grain heat preservation sand syrup be a wall out of the building of outside heat preservation, have of glue to stick noodles brick on the heat preservation material, keep noodles brick from open crack, empty drum, this text gather the benzene grain heat preservation sand syrup top to glue to stick noodles brick to carry on study to the gum powder.
【Key words】Heat preservation sand syrup;The outside heat preservation system outside the wall;Noodles brick
建筑外墙装饰工程中贴面砖80年代初期已广泛应用，因其具有比建筑外墙弹性涂料装饰效果美、耐污染性能好、使用过程中维护费用低，等优点，应用面越来越广。饰面砖其传统做法是在粉刷层表面和混凝土墙体表面进行粘贴。近年来，随着保温材料的广泛应用，大多数在保温墙体上粘贴面砖。随着时间的推移，面砖饰面工程出现了许多质量问题，主要问题是沿面砖缝出现开裂、面砖脱落和渗水。因此在外保温层上贴面砖，其使用安全性不能不引起人们的担忧。
当前，有许多种保温层贴面砖的做法，其中胶粉聚苯颗粒保温砂浆外墙粘贴面砖技术在行业标准《胶粉聚苯颗粒外墙外保温系统》JG158-2004中作出了明确规定，胶粉聚苯颗粒外墙外保温系统粘贴面砖技术的基本构造，以胶粉聚苯颗粒为保温层、抗裂砂浆、钢丝网、抗裂砂浆为基体建筑外墙外保温墙面上粘贴面砖，尤其是高层建筑，其安全性为首要要求。一般情况下，饰面粘贴面砖主要考虑保温系统内各层材料的粘结强度是否符合规范标准的规定值。与基层墙体不同，外保温系统由于密度小、强度低的保温层，其形成的复合墙体往往呈现软质基底的特征。同时外保温系统置于建筑结构外层，热应力、火、水或水蒸气、风压、地震等外界作用力直接作用于其表面，需要采取相应措施，使建筑物和保温系统本身防止出现开裂、起鼓、脱落等质量事故。
1. 影响外墙外保温墙面粘贴面砖质量的主要因素
1.1 在保护保温层的前提下，使外保温系统形成一个整体，转移面砖饰面层负荷作用体，改善面砖粘贴层的强度。
1.2 要考虑外保温材料的压折比、粘结强度、耐候稳定性等指标以及整个外保温系统材料的形变，或其他应力。
1.3 外保温材料的抗渗性以及系统的透气性，避免冻融破坏而导致面砖掉落。
1.4 外保温系统的防火等级，避免火灾等意外事故发生后产生空腔，外保温系统丧失整体性在面砖饰面的自重重力的影响下大面积脱落。
1.5 外保温系统的抗震和抗风压能力，避免偶发事故出现后的水平方向作用力对外保温系统的破坏。
2. 系统性能检测
系统性能检测是了解外保温粘贴面砖质量的手段，因此要保证高层建筑外墙外保温粘贴面砖的安全性，保证系统应通过以下几个方面的检测
2.1 系统耐候性能试验：考验保温系统承受聚热、聚冷的能力。
2.2 系统吸水量性能试验: 考验保温系统吸水的能力。
2.3 系统抗风荷载性能试验: 考验保温系统抵抗正负风压的能力。
2.4 系统耐冻融性能试验: 考验保温系统承受抗冻融的能力。
2.5 系统抗冲击性能试验: 考验保温系统抗冲击破坏的能力。
2.6 系统抗拉强度试验: 考验保温系统的粘结强度。
2.7 系统抗不透水性试验: 考验保温系统的拒水能力。
2.8 系统水蒸气渗透性能试验: 考验保温系统的拒水能力。
2.9 系统抗震性能试验: 考验保温系统的对设防地震裂度的能力。
2.10 系统防火性能试验: 考验保温系统的对设火灾等意外事故造成面砖脱落。
2.11 系统面砖勾缝料渗水性能试验: 考验保温系统中面砖勾缝料渗水能力。
2.12 系统耐磨损性能试验: 考验保温系统耐磨损的能力
2.13 系统饰面砖粘结强度性能试验：考验保温系统饰面砖的粘结强度。
在《胶粉聚苯颗粒外墙外保温系统》JG158-2004中明确规定的强制性条文，外墙外保温系统应经大型耐候性试验验证。对面砖饰面外保温系统，还应经抗震试验验证并确保其在设防裂度等级地震下面砖饰面及外保温系统无脱落。
3. 胶粉聚苯颗粒保温砂浆外墙保温系统粘贴面砖的“增强结构”的选择
《胶粉聚苯颗粒外墙外保温系统》JG158-2004中明确规定，面砖饰面采用“热镀锌电焊网”，涂料饰面采用“耐碱玻纤网格布”。
假如以“耐碱玻纤网格布”为增强材料，虽然有效的提高了抗裂砂浆的抗裂效果，但外饰面为面砖饰面时，对基层强度的增强作用不大，不能有效的分散面砖装饰层荷载作用对基层的作用。荷载仍然作用地强度较低的保温浆层上，对整个系统不够安全，不仅如此，由于玻纤网格布的网孔小，与砂浆握裹不好，玻纤网形成隔离层，只是增强了平行方向的抗拉强度，对垂直方向的强度无明显改善，而且整个面砖粘贴在抹面砂浆和复合玻纤网格布形成的抗裂层上，与基层没有任何连接，整个保温系统形成两块，面砖上的荷载不能传递到基层结构上，存在面砖层与抗裂层整体脱落的危险，因此面砖饰面不宜采用 “耐碱玻纤网格布”作为增强结构。
采用“热镀锌电焊网” 作为增强结构时，热镀锌电焊网铺设于抗裂砂浆中，使抗裂砂浆防护层得到有效加固，再通过塑料膨胀管将电焊网与基层结构直接固定，转移了面层负荷作用，将面层荷载转移到基层界面，此时保温层得到有效保护，当受到外力作用时破坏发生在抗裂防护层上，并很好的被防护层吸收，由于钢丝网与抗裂砂浆有很好的握裹力，钢丝网合理增强了水平方向与垂直方向抗拉强度，极大改善了面砖粘结基层的强度，因此采用“热镀锌电焊网” 作为增强结构时能有效兼顾抗裂性能与基层与面砖对基层强度要求之间的统一，满足保温系统的稳定性、安全性和耐久性的要求。
4. 材料的技术要求
在保温系统面层上粘结面砖，与在混凝土基层粘贴面砖条件不同，因此选择外保温砂浆、抗裂砂浆、面砖粘结剂时除要考虑耐候性、耐水性、耐老化性能，常温施工等因素外，还必须考虑不同硬度、密度的材料在使用过程中由温度变化而引起的不同形变差异而造成的内应力。选用粘结剂应通过自身的形变消除两种质量、硬度、热工性能完全不同的材料的形变差异，才能确保硬度大、密度高、弹性模量大、可变形性低的面砖在硬度低、密度小、弹性模量小、可变形性高的保温层上不脱落。为了保证系统的粘结强度达到现行国家标准规范要求，同时为了保证材料必要的可变形性和较低的弹性模量，抗裂砂浆、面砖粘结剂的可变形性宜控制在≥5‰，压折比＜3.0。
钢丝网应为热镀锌电焊网、锚栓应为塑料材料，其规格要求应满足设计要求，还必须满足防腐性能、耐久性能的要求。面砖勾缝材料也要满足柔韧性、防水抗渗要求来消除温度变形的危害。尽可能使用低弹性模量、小尺寸的瓷砖。
5. 结束语
在外墙保温面层粘贴面砖时首先符合安全性能要求，对保温砂浆进行现场强度检测合格后方可进行面砖粘贴。胶粉聚苯颗粒保温砂浆外墙粘贴面砖时应充分充分考虑其影响因素，设置伸缩缝，可防止墙体结构变形及外墙饰面砖本身温度变形导致的开裂和脱落采用柔性防水材料嵌缝，可吸收变形，增加饰面的抗渗性。饰面砖接缝过小，则在温度应力作用下易引起脱落。规程定为“宽度不应小于5mm”。 有研究成果表明：要减小界面上因温差引起的剪应力，防止瓷砖脱落，应尽可能使用柔性胶粘剂；要有适当的胶层厚度、良好的施工技术方能保证面砖粘结质量。
参考文献
［1］ 《胶粉聚苯颗粒外墙外保温系统》JG158-2004
［2］ 《外墙外保温工程技术规程》JGJ144-2004
［文章编号］1619-2737（2010）11-20-241
【关键词】保温砂浆；外墙外保温系统；面砖
The gum powder gatherbenzene grain heat preservation sand wall outsidesyrupstick noodles brick analysis
Xiao Jian-ming,Xi Jun-feng
(taixin city zhongxin construction engineering quality examination center limited company Taixin Jiangsu 225400)
【Abstract】Majority engineering usage gum powder's gather the benzene grain heat preservation sand syrup be a wall out of the building of outside heat preservation, have of glue to stick noodles brick on the heat preservation material, keep noodles brick from open crack, empty drum, this text gather the benzene grain heat preservation sand syrup top to glue to stick noodles brick to carry on study to the gum powder.
【Key words】Heat preservation sand syrup;The outside heat preservation system outside the wall;Noodles brick
建筑外墙装饰工程中贴面砖80年代初期已广泛应用，因其具有比建筑外墙弹性涂料装饰效果美、耐污染性能好、使用过程中维护费用低，等优点，应用面越来越广。饰面砖其传统做法是在粉刷层表面和混凝土墙体表面进行粘贴。近年来，随着保温材料的广泛应用，大多数在保温墙体上粘贴面砖。随着时间的推移，面砖饰面工程出现了许多质量问题，主要问题是沿面砖缝出现开裂、面砖脱落和渗水。因此在外保温层上贴面砖，其使用安全性不能不引起人们的担忧。
当前，有许多种保温层贴面砖的做法，其中胶粉聚苯颗粒保温砂浆外墙粘贴面砖技术在行业标准《胶粉聚苯颗粒外墙外保温系统》JG158-2004中作出了明确规定，胶粉聚苯颗粒外墙外保温系统粘贴面砖技术的基本构造，以胶粉聚苯颗粒为保温层、抗裂砂浆、钢丝网、抗裂砂浆为基体建筑外墙外保温墙面上粘贴面砖，尤其是高层建筑，其安全性为首要要求。一般情况下，饰面粘贴面砖主要考虑保温系统内各层材料的粘结强度是否符合规范标准的规定值。与基层墙体不同，外保温系统由于密度小、强度低的保温层，其形成的复合墙体往往呈现软质基底的特征。同时外保温系统置于建筑结构外层，热应力、火、水或水蒸气、风压、地震等外界作用力直接作用于其表面，需要采取相应措施，使建筑物和保温系统本身防止出现开裂、起鼓、脱落等质量事故。
1. 影响外墙外保温墙面粘贴面砖质量的主要因素
1.1 在保护保温层的前提下，使外保温系统形成一个整体，转移面砖饰面层负荷作用体，改善面砖粘贴层的强度。
1.2 要考虑外保温材料的压折比、粘结强度、耐候稳定性等指标以及整个外保温系统材料的形变，或其他应力。
1.3 外保温材料的抗渗性以及系统的透气性，避免冻融破坏而导致面砖掉落。
1.4 外保温系统的防火等级，避免火灾等意外事故发生后产生空腔，外保温系统丧失整体性在面砖饰面的自重重力的影响下大面积脱落。
1.5 外保温系统的抗震和抗风压能力，避免偶发事故出现后的水平方向作用力对外保温系统的破坏。
2. 系统性能检测
系统性能检测是了解外保温粘贴面砖质量的手段，因此要保证高层建筑外墙外保温粘贴面砖的安全性，保证系统应通过以下几个方面的检测
2.1 系统耐候性能试验：考验保温系统承受聚热、聚冷的能力。
2.2 系统吸水量性能试验: 考验保温系统吸水的能力。
2.3 系统抗风荷载性能试验: 考验保温系统抵抗正负风压的能力。
2.4 系统耐冻融性能试验: 考验保温系统承受抗冻融的能力。
2.5 系统抗冲击性能试验: 考验保温系统抗冲击破坏的能力。
2.6 系统抗拉强度试验: 考验保温系统的粘结强度。
2.7 系统抗不透水性试验: 考验保温系统的拒水能力。
2.8 系统水蒸气渗透性能试验: 考验保温系统的拒水能力。
2.9 系统抗震性能试验: 考验保温系统的对设防地震裂度的能力。
2.10 系统防火性能试验: 考验保温系统的对设火灾等意外事故造成面砖脱落。
2.11 系统面砖勾缝料渗水性能试验: 考验保温系统中面砖勾缝料渗水能力。
2.12 系统耐磨损性能试验: 考验保温系统耐磨损的能力
2.13 系统饰面砖粘结强度性能试验：考验保温系统饰面砖的粘结强度。
在《胶粉聚苯颗粒外墙外保温系统》JG158-2004中明确规定的强制性条文，外墙外保温系统应经大型耐候性试验验证。对面砖饰面外保温系统，还应经抗震试验验证并确保其在设防裂度等级地震下面砖饰面及外保温系统无脱落。
3. 胶粉聚苯颗粒保温砂浆外墙保温系统粘贴面砖的“增强结构”的选择
《胶粉聚苯颗粒外墙外保温系统》JG158-2004中明确规定，面砖饰面采用“热镀锌电焊网”，涂料饰面采用“耐碱玻纤网格布”。
假如以“耐碱玻纤网格布”为增强材料，虽然有效的提高了抗裂砂浆的抗裂效果，但外饰面为面砖饰面时，对基层强度的增强作用不大，不能有效的分散面砖装饰层荷载作用对基层的作用。荷载仍然作用地强度较低的保温浆层上，对整个系统不够安全，不仅如此，由于玻纤网格布的网孔小，与砂浆握裹不好，玻纤网形成隔离层，只是增强了平行方向的抗拉强度，对垂直方向的强度无明显改善，而且整个面砖粘贴在抹面砂浆和复合玻纤网格布形成的抗裂层上，与基层没有任何连接，整个保温系统形成两块，面砖上的荷载不能传递到基层结构上，存在面砖层与抗裂层整体脱落的危险，因此面砖饰面不宜采用 “耐碱玻纤网格布”作为增强结构。
采用“热镀锌电焊网” 作为增强结构时，热镀锌电焊网铺设于抗裂砂浆中，使抗裂砂浆防护层得到有效加固，再通过塑料膨胀管将电焊网与基层结构直接固定，转移了面层负荷作用，将面层荷载转移到基层界面，此时保温层得到有效保护，当受到外力作用时破坏发生在抗裂防护层上，并很好的被防护层吸收，由于钢丝网与抗裂砂浆有很好的握裹力，钢丝网合理增强了水平方向与垂直方向抗拉强度，极大改善了面砖粘结基层的强度，因此采用“热镀锌电焊网” 作为增强结构时能有效兼顾抗裂性能与基层与面砖对基层强度要求之间的统一，满足保温系统的稳定性、安全性和耐久性的要求。
4. 材料的技术要求
在保温系统面层上粘结面砖，与在混凝土基层粘贴面砖条件不同，因此选择外保温砂浆、抗裂砂浆、面砖粘结剂时除要考虑耐候性、耐水性、耐老化性能，常温施工等因素外，还必须考虑不同硬度、密度的材料在使用过程中由温度变化而引起的不同形变差异而造成的内应力。选用粘结剂应通过自身的形变消除两种质量、硬度、热工性能完全不同的材料的形变差异，才能确保硬度大、密度高、弹性模量大、可变形性低的面砖在硬度低、密度小、弹性模量小、可变形性高的保温层上不脱落。为了保证系统的粘结强度达到现行国家标准规范要求，同时为了保证材料必要的可变形性和较低的弹性模量，抗裂砂浆、面砖粘结剂的可变形性宜控制在≥5‰，压折比＜3.0。
钢丝网应为热镀锌电焊网、锚栓应为塑料材料，其规格要求应满足设计要求，还必须满足防腐性能、耐久性能的要求。面砖勾缝材料也要满足柔韧性、防水抗渗要求来消除温度变形的危害。尽可能使用低弹性模量、小尺寸的瓷砖。
5. 结束语
在外墙保温面层粘贴面砖时首先符合安全性能要求，对保温砂浆进行现场强度检测合格后方可进行面砖粘贴。胶粉聚苯颗粒保温砂浆外墙粘贴面砖时应充分充分考虑其影响因素，设置伸缩缝，可防止墙体结构变形及外墙饰面砖本身温度变形导致的开裂和脱落采用柔性防水材料嵌缝，可吸收变形，增加饰面的抗渗性。饰面砖接缝过小，则在温度应力作用下易引起脱落。规程定为“宽度不应小于5mm”。 有研究成果表明：要减小界面上因温差引起的剪应力，防止瓷砖脱落，应尽可能使用柔性胶粘剂；要有适当的胶层厚度、良好的施工技术方能保证面砖粘结质量。