Three novel triazine-based charring-foaming agents (M2-CFA,M4-CFA,and M6-CFA) were synthesized successfully with only water as the solvent and were characterized by FT-IR and thermal gravimetric analysis (TGA).These three charring-foaming agents and the byproduct 944-by were employed to study the effectiveness of the novel intumescent flame retardant dopant on the fire retardancy of polypropylene (PP) investigated through UL-94 and limiting oxygen index (LOI) tests.TGA results showed that the M4-CFA presented good char formation ability (char residue: 26.8% at 700 ℃).It was found that the sample with a 2/1 mass ratio of APP to M4-CFA exhibited the best flame retardancy among all the PP composites: 35.5% LOI and a V-0 rating of UL-94.Additionally,the microstructure and morphology of char residues were further studied by XRD,Raman spectroscopy and SEM.
Three novel triazine-based charring-foaming agents (M2-CFA, M4-CFA, and M6-CFA) were synthesized successfully with only water as the solvent and were characterized by FT-IR and thermal gravimetric analysis (TGA) -foaming agents and the byproduct 944-by were employed to study the effectiveness of the novel intumescent flame retardant dopant on the fire retardancy of polypropylene (PP) investigated through UL-94 and limiting oxygen index (LOI) tests. TGA results showed that the M4-CFA presented good char formation ability (char residue: 26.8% at 700 ° C) .It was found that the sample with a 2/1 mass ratio of APP to M4-CFA exhibited the best flame retardance among all the PP composites: 35.5 % LOI and a V-0 rating of UL-94. Additionally, the microstructure and morphology of char residues were further studied by XRD, Raman spectroscopy and SEM.