In order to improve the purifying efficiency of RJ6 flux, 5% (mass fraction) GdCl3 was introduced into the flux for refining Mg-10Gd-3Y-0.5Zr (GW103K) alloy. Th
【机 构】
：
National Engineering Research Center of Light Alloy Net Forming,State Key Laboratory of Metal Matrix
论文部分内容阅读
In order to improve the purifying efficiency of RJ6 flux, 5% (mass fraction) GdCl3 was introduced into the flux for refining Mg-10Gd-3Y-0.5Zr (GW103K) alloy. The results show that the RJ6 flux containing 5% GdCl3 exhibits better adsorption ability to nonmetallic inclusions than the one without GdCl3. Moreover, the mechanical, corrosion properties and fluidity of the alloy refined with RJ6 flux and RJ6 flux containing 5% GdCl3 were investigated, respectively. It is found that these properties are improved to a certain degree due to the removal of nonmetallic inclusions in the alloy. Thermodynamic analysis and surface tension experiments indicate that the main reason can be ascribed to the decrease of the surface tension of the flux with 5% GdCl3, which promotes the combination of flux and nonmetallic inclusions.
其他文献
在全球化的进程中,自然文化遗产的经济价值明显地提升了,其经济价值和其他价值之间的矛盾也变得越来越突出。如果能够有效地利用自然文化遗产资源的比较优势来发展旅游业,就
在农业结构调整、生态退耕、建设占用和自然灾毁综合影响下,我国耕地总量逐年减少,国家虽然采取了一系列严格的管理措施,仍难以扭转耕地持续减少的态势.针对这一难题,本研究
目的 探讨含钍稀土混合粉尘对职业暴露人员血清细胞因子白细胞介素2、白细胞介素6和肿瘤坏死因子以及血液学常规的影响.方法 采用放射免疫法分析血清细胞因子白细胞介素2、白
综述SiC纤维增强钛基复合材料界面强度的影响因素、微观实验测试技术以及数值模拟技术.在此基础上着重分析了微观实验测试技术与数值模拟技术存在的问题,指出了界面强度定量
目的 阐明陕南燃煤型砷皮肤损伤的危险因素.方法 依据地方性砷中毒的诊断标准对陕西省安康市汉滨区2个村的198例居民进行现况调查.在单因素分析剔除对燃煤型砷皮肤损伤相关性
针对Ti-6Al-4V合金在加工和服役过程中的损伤特点,对Ti-6Al-4V合金锻件的3种典型误加工缺陷--槽缺陷、面缺陷和体缺陷进行了激光快速修复研究.激光修复区与锻件基体形成致密
The effects of two kinds of heat treatments T4 (solution treatment) and T6 (aging treatment) on the corrosion behaviors of Mg-3Zn magnesium alloy were studied b
The microstructure and mechanical properties of Mg-xSn (x=3, 7 and 14, mass fraction, %) alloys extruded indirectly at 300 ℃ were investigated by means of opti
Stress intensity factors of thin AZ31B magnesium alloy sheet under biaxial tension loading were analyzed by modified Dugdale model. K-values with crack angle of
The influence of impurities on damping capacities of ZK60 magnesium alloys in the as-cast, as-extruded and T4-treated states was investigated by dynamically mec