4)新工艺方法:有郭射宇博士(江苏吴江科技创业园)提出的气流溅射法、德国安铝使用的热熔胶法等,相关图谱如图6所示。由图6可知,郭射宇博士提出的气流溅射法制备的涂层α=0.92,εn=0.06(80℃),德国安铝热熔胶样品α=0.91,εn=0.31。样品由殷志强、周小雯等人采用PE Lambda 950和美国“dts”仪在北京卫星厂检测,测试显示涂层的性能不良。2.6吸收涂层反射曲线
4) The new process: Dr. Guo Dr. Yu (Jiangsu Wujiang Technology Pioneer Park) proposed by the sputtering method, the German aluminum used hot melt adhesive method, the relevant map shown in Figure 6. As can be seen from FIG. 6, the coatings prepared by the air-jet sputtering method proposed by Dr. Guo Shuiyu are α = 0.92 and εn = 0.06 (80 ° C). The German aluminum hot melt adhesive samples α = 0.91 and εn = 0.31. Samples by the Yin Zhiqiang, Zhou Xiaowen and others using PE Lambda 950 and the United States “dts ” instrument in the Beijing Satellite Factory testing, the test showed poor performance of the coating. 2.6 absorption coating reflection curve