Amorphous Mg55Ni35Si10 powders are fabricated by using a mechanical alloying technique. The amorphous powders are found to exhibit a relatively high crystallization temperature of 380℃. The as-milled amorphous Mg55Ni35Si10 powders are consolidated successfully into bulk body by vacuum hot pressing technique. Limited nanocrystallization is noticed. The Vickers microhardness range of the Mg55Ni35Si10 bulk sample is 7834 to 8048 Mpa. Its bending strength and compressive strength are 529 Mpa and 1466 Mpa, respectively.