Ferromagnetic Fe3O4 nanoparticles were synthesized and then self-assembled into microparticles via a solvothermal method, using FeCI3.6H2O as the iron source, sodium oleate as the surfactant, and ethylene glycol as the reducing agent and solvent. The obtained Fe3O4 microparticles were characterized by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy and vibrating sample magnetometer (VSM). The size and morphology of the particles were examined using transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The Fe3O4 microparticles of nearly monodisperse diameters, controllable in the range of 120-400 nm, consist of assemblies of Fe3O4nanoparticles with a diameter of 22 nm. The effects of reaction time, amount of surfactant and NaAc on the products were discussed. Interestingly, by using the pre-synthesized Fe3O4 microparticles as the growth substrates, spherical and smooth-looking Fe3O4 microparticles with average diameter of lμmwere obtained. A plausible formation process was discussed.