【摘 要】
：
Characterizations of phases in Mg-10%Y-5%Gd-2%Zn-0.5%Zr (WGZ1052) alloy during heat treatments were investigated by OM, XRD, SEM and EDS. The mechanisms of micr
【机 构】
：
National Engineering Research Center of Light Alloys Net Forming,Grikin Advanced Materials Co.
论文部分内容阅读
Characterizations of phases in Mg-10%Y-5%Gd-2%Zn-0.5%Zr (WGZ1052) alloy during heat treatments were investigated by OM, XRD, SEM and EDS. The mechanisms of microstructure evolution were discussed. The results show that, after high temperature heat treatments, the Mg12ZnY phases still exist. During solution-treatment at 535 ℃, the amount of the long-period stacking order structures decreases. At 545 ℃ for 20 h and 24 h, there are still remnant Mg12ZnY compounds in the Mg matrix, the shape of which does not change and the amount does not decrease obviously.
其他文献
Several methods for analysis of dissolved total phosphorus in seawater were reviewed. Discussions were focused on UV irradiation and persulphate oxidation metho
The microstructure and crystallographic texture characteristics of an extruded ZK60 Mg alloy subjected to cyclic extrusion and compression (CEC) up to 8 passes
The physical characteristics and microstructure of the fluoride film formed during activation were investigated using SEM, XPS and SAM, and its stability in ele
Process of warm tube hydroforming was experimentally investigated for forming an AZ31B magnesium alloy tubular part with a large expansion ratio. Effects of tem
The development of the phytoplankton community was studied in the Jiaozhou Bay during the spring to neap tide in August 2001, through three cruises and a 15 d c
The polyurethane/polyacrylonitrile ( PU/PAN ) and polyurethane/cellulose acetate (PU/CA) blend ultra filtration membranes were prepared based on LoebSourirajan
Data collection, factor composition, nappe analysis and integrative simulation of natural geographical factors in Erlong Lake watershed have been carried out ba
The working principle of LFEC(Low frequency electromagnetic casting) process developed in Northeastern University, China was introduced and the metallurgical re
Two kinds of unidirectional PAN M40 carbon fiber (55%, volume fraction) reinforced 6061Al and 5A06Al composites were fabricated by the squeeze-casting technolog