【摘 要】
：
在熔盐体系相图指导下研制出以脲和硫氰酸铵 (钾 )为主体的高分子固体电解质 ( PSE) ,其室温电导率分别为 1 .2 0× 1 0 - 2和 2 .6 5× 1 0 - 3 S/cm.考察了影响该 PSE电导
【机 构】
：
陕西理工学院化学系,陕西理工学院化学系 汉中723000,汉中723000
论文部分内容阅读
在熔盐体系相图指导下研制出以脲和硫氰酸铵 (钾 )为主体的高分子固体电解质 ( PSE) ,其室温电导率分别为 1 .2 0× 1 0 - 2和 2 .6 5× 1 0 - 3 S/cm.考察了影响该 PSE电导率的因素 ,讨论了 PSE的导电机理 .结果表明 ,所研制的 PSE为无定形固熔体 ,主要通过硫氰酸盐的电离导电 ,电导率 -温度关系服从 VTF方程 .
Under the guidance of the phase diagram of molten salt system, the polymer solid electrolyte (PSE) with urea and ammonium thiocyanate (potassium) as the main component has been developed and its conductivity at room temperature is respectively 1.20 × 10 -2 and 2.6 5 × 10 3 S / cm. The factors that affect the conductivity of PSE were investigated and the conduction mechanism of PSE was discussed. The results showed that PSE was amorphous solid melt mainly through the ionization conductivity of thiocyanate , The conductivity-temperature relationship obeys the VTF equation.
其他文献
The reactions of 2,3-dihydro-1,5-benzothiazepines with ethoxycarbonylcarbene undergo complex rearrangements to produce ring-opening and ring contraction product
作为电力信息学的基础理论之一,将电力系统的分析决策过程看成是一个广义的信息重建过程.针对电力系统中普遍的概率型信息,从传统的信息理论出发,建立了广义的信道模型,提出
研究了用电子回旋共振(ECR)等离子体增强金属有机物化学气相沉积(PEMOCVD)技术在Si(001)衬底上,低温(620～720℃)下GaN薄膜的直接外延生长及晶相结构.高分辨透射电镜(HRTEM)和X
有别于以往对颗粒团聚问题宏观而粗略的研究,提出从微观受力的角度探索颗粒团聚及破碎的机理。对循环流化床内运动颗粒的全受力分析表明,一般流化条件下,影响颗粒团聚及破碎
应用广义胞映射图论(GCMD)方法,研究两参量正弦强迫振子的双重激变现象,确定了两参量平面上的双重激变尖点,在这个尖点上两条边界激变曲线和两条内部激变曲线相汇交,四种不同
荧光染料作为分子探针用于核酸的定量测定和构象分析一直备受关注[1]. 已有数十种荧光染料被应用[2,3], 如溴化乙锭早期常用作DNA探针[4,5], 因其有很强的致癌性, 目前已很少
以负三价、五啮的Ⅳ-乙酰水杨酰肼(ashz3-)作为配体,合成了二个大环六核氮杂金属冠醚[MnⅢ6(ashz)6(MeOH)6]@6Me0H(1)和[MnⅢ6(ashz)6(DMF)6]@3DMF(2).晶体学数据是:配合物1,
用线性变换方法推导了二维正方结构正n边形直柱光子晶体的带隙计算公式 .采用线性变换方法可以简单地处理平面波展开方法中ε- 1 (r)的Fourier变换系数 ,使得相应的带隙计算
用量子理论定量计算了Er3Ga5O12在强磁场作用下,温度为4.2K,外磁场沿着[001],[100],[110]和[111]四个方向的磁化强度.可以看出,磁化强度随着外磁场呈很强的各向异性,而在低温
利用指数矩阵精细算法及状态方程直接积分法,讨论了求解动力响应问题的时程积分方式.通过选择代数精度高的Cotes积分,得出了计算精度非常高的动力响应结果.采用减缩主从自由