用定群血清流行病学方法观察HFRS疫苗效果考核现场对照组人群隐性感染情况。采用IFAT检则血清中HFRSIgG抗体,分析不同性别和年龄人群的隐性感染及感染后抗体水平变化情况。结果,HFRS年感染率为229%,在不同性别和年龄组中未见显著差异;32名隐性感染者HFRS抗体转阴率4688%,HFRS抗体上升率达2500%,在不同HFRS抗体滴度、性别和年龄组中未见显著差异。此观察结果为疫苗现场效果评价提供一些背景资料。 Serological epidemiological methods were used to observe the effect of HFRS vaccination in the field control group. IFRS test serum HFRSIgG antibody analysis of different gender and age groups, latent infection and antibody levels after infection changes. As a result, the annual infection rate of HFRS was 229%, and there was no significant difference among different sexes and age groups. The negative rate of HFRS antibody in 32 latent infections was 4688%, and the rate of HFRS antibody increased was 2500% There were no significant differences in titers, sexes and age groups for different HFRS antibodies. This observation provides some background information for the evaluation of the efficacy of vaccines.
其他文献
本文针对ER70S-6盘条在用户使用过程中出现拉拔断裂的原因进行分析,认为线材的组织缺陷是拉拔断裂的主要原因,并提出相应的解决措施,减少拉丝断裂频率。
针对棒一车间产品称量入库存在的问题,开发了电子称量管理系统,并应用在岗位操作中,加快了型棒材厂信息化建设的进程,改善了职工的工作条件,提高了生产效率,对改善各项经济技术指标
H08A焊条钢属于低碳、低硅易拉丝钢,主要用途为拉丝焊条。现介绍扭线材轧钢生产线轧制工艺特点,生产流程、工艺参数,以及质量要求和化学成分,
简要介绍无头焊接轧制的设备及工艺过程,并针对国内企业的实际使用状况,提出了亟待解决的问题。
针对冷床冷却能力不足的问题。采用引进的THERMEX轧后穿水设备进行间断式弱冷,不仅降低了钢筋剪切时温度200℃左右,提高了钢筋剪切质量,而且有限度提高了钢筋的力学性能,屈服强度
本文介绍了唐钢AWSER70S-6CO2气保焊丝用钢盘条的生产情况,及碳、锰、硅含量对抗拉强度的影响和拉拔断产生的原因,吐丝温度和冷却速度对组织性能的影响。
结合楔横轧变形理论,通过理化分析验证楔横轧对材料要求。分析了楔横轧心部缺陷的产生机理,理化检验表明:原材料中存在原始裂纹。要求连铆机尽可能采用结晶器电磁搅拌,较低的过热
会议
本文介绍了高速线材生产中新出现的加热炉燃烧控制,热送热装、无头轧制、控轧控冷、减径定径轧制以及信息化管理等新技术的内容、目的、方法。并结合实际在应用方面做了讲解。
主要利用Nb的沉淀强化机制,通过合理调整C、Mn成分,开发了Nb微合金化HRB400热轧钢筋生产技术,除微合金化方式不同外,冶炼、轧制工艺与低合金生产工艺基本相同,适合棒线生产线装备
本文通过一系列实验室研究工作,从微观和宏观两方面证实了酸性表面调整处理有助于提高彩涂板的抗剥离性能和耐蚀能力。