【摘 要】
：
采用腐蚀试验测试了钢筋HRB400在模拟混凝土孔隙液(3.5wt%NaCl溶液)中的腐蚀率,并采用拉伸试验测试了钢筋腐蚀前后的力学性能。结果表明,随着腐蚀时间从240h增加到720h,钢筋
论文部分内容阅读
采用腐蚀试验测试了钢筋HRB400在模拟混凝土孔隙液(3.5wt%NaCl溶液)中的腐蚀率,并采用拉伸试验测试了钢筋腐蚀前后的力学性能。结果表明,随着腐蚀时间从240h增加到720h,钢筋的腐蚀率逐渐增加,腐蚀逐渐加重;随着腐蚀时间(腐蚀率)的增加,钢筋屈服强度和抗拉强度均逐渐下降,而伸长率先下降后上升。
The corrosion rate of steel HRB400 in simulated concrete pore fluid (3.5wt% NaCl solution) was tested by corrosion test. The tensile test was used to test the mechanical properties of steel bar before and after corrosion. The results show that as the corrosion time increases from 240h to 720h, the corrosion rate increases and the corrosion gradually aggravates. With the increase of corrosion time (corrosion rate), the yield strength and tensile strength of the steel decrease gradually, while the elongation first Fall after rising.
其他文献
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
多发性开放性骨折是一种危急重症,病情较重,并发症多,多伴有低血容量性休克,病死率较高,有效的静脉通道是纠正休克的关键,熟练的护理技术是抢救成功的保证,对患者的预后至关
人类对于自然资源的利用往往会陷入“大力开发—认识错误—纠正错误”的循环中，以近代人类发明使用的多种化学物质为例，化学工程师发明利用了它们，却在使用中重新认识到对自然和人类自身造成的危害，最后不得不纠正这一错误，采取封存和回收等纠正办法。 在电子电气产业、汽车制造业等与人们生活息息相关的产业，这种对有害物质的限制使用，甚至禁止生产和使用的潮流已经在全世界普及多年。 在船舶行业，这种潮流同样开始涌
目的:观察槲皮素(Que)对单侧输尿管梗阻大鼠肾脏病理和α-平滑肌肌动蛋白(α-SMA)表达的影响,探讨槲皮素对肾间质纤维化的保护作用及作用机制.方法:采用单侧输尿管结扎(UUO)
采用单辊甩带法制备出(Ni0.5Co0)6Nb25Ti15非晶带材,利用X射线衍射和扫描差热分析对该非晶带材的晶化动力学过程进行研究,并用Kissinger方程计算其晶化激活能.结果表明:(Ni0.
借助光学显微镜和SEM电镜观察,运用磨损试验手段及对比研究法,研究了高硼低碳耐磨合金的磨料磨损性能.结果表明,在中、低冲击工况下,高硼低碳耐磨合金的磨损质量损失、相对磨
王行宽,男,中共党员,1939年3月出生于名医辈出的江苏省镇江市,系全国老中医药专家学术经验继承第2、3、4、5批指导老师,全国名老中医传承工作室专家,享受国务院特殊津贴专家,
介绍了电解液喷射沉积制备泡沫镍的原理,讨论了相关电沉积参数对电沉积速度的影响,并且对影响因素进行了基础研究.结果表明,电流密度及电解液喷射速度与沉积速度呈线性关系,