TiN coating was prepared by reactive plasma spraying in the Ar and N2 containing plasma jet. The results of XRD show that the TiN coating consists of TiN and Ti3O, neither Ti2N nor TiO2 phases. The toughening mechanism was characterized by analyzing the SEM morphologies of the TiN coating′s indentation of microhardness and fracture surfaces. The results indicate that the coating possesses a high toughness. The adhesion strength among the TiN layers is 25.88 MPa, which is slightly lower than that of the Ni/Al bonding coating. The oxidation process of the RPS TiN coating is TiN→Ti3O→TiO2.
TiN coating was prepared by reactive plasma spraying in the Ar and N2 containing plasma jet. The results of XRD show that the TiN coating consists of TiN and Ti3O, neither Ti2N nor TiO2 phases. The toughening mechanism was characterized by analyzing the SEM morphologies of the The results indicate that the coating possesses a high toughness. The adhesion strength among the TiN layers is 25.88 MPa, which is slightly lower than that of the Ni / Al bonding coating. The oxidation process of the RPS TiN coating is TiN → Ti3O → TiO2.