采用硬脂酸凝胶法制备磁性NiCo2O4纳米颗粒.通过红外(FT-IR)、热重(TG)对前驱物进行分析;X-射线粉末衍射(XRD)研究了煅烧温度对NiCo2O4晶体形成的影响;透射电镜(TEM)、振动试
【机 构】
：
福建师范大学材料科学与工程学院,福建省高分子材料重点实验室福建,
论文部分内容阅读
采用硬脂酸凝胶法制备磁性NiCo2O4纳米颗粒.通过红外(FT-IR)、热重(TG)对前驱物进行分析;X-射线粉末衍射(XRD)研究了煅烧温度对NiCo2O4晶体形成的影响;透射电镜(TEM)、振动试样磁强计(VSM)对产物的形貌及磁性能进行表征.结果表明,380℃保温6 h可以获得单一晶相的NiCo2O4尖晶石纳米颗粒,粒度分布较窄,平均粒径约为9 nm,矫顽力为147 Oe,饱和磁化强度为2.22emu.g-1.
Magnetic NiCo2O4 nanoparticles were prepared by stearic acid gel method.The precursors were analyzed by FT-IR and TG, and the effect of calcination temperature on the formation of NiCo2O4 crystal was investigated by X-ray powder diffraction (XRD) (TEM) and vibrating sample magnetometer (VSM) were used to characterize the morphology and magnetic properties of the product.The results showed that single phase NiCo2O4 spinel nanoparticles were obtained at 380 ℃ for 6 h, and the particle size distribution Narrow, average particle size of about 9 nm, coercivity of 147 Oe, saturation magnetization of 2.22emu.g-1.
其他文献
目的:克隆小鼠CXCR4基因并建立其慢病毒表达系统。方法:设计合成PCR引物,从小鼠骨髓有核细胞来源的cDNA中扩增并克隆小鼠CXCR4基因的编码区。构建CX-CR4-IRES-GFP表达单元后
目的 探讨腹腔镜下保留盆腔自主神经(PANP)的直肠癌根治术对患者术后排尿功能的保护效果.方法 对中山大学附属第三医院2005年11月至2007年10月间住院的139例中低位直肠癌患者
目的 分析研究我国北方地区假肥大性肌营养不良[分为杜克肌营养不良(DMD)和贝克肌营养不良(BMD)]患者抗肌萎缩蛋白基因突变的类型,断裂点的分布,并为临床应用奠定基础.方法
凋亡抑制因子Survivin是凋亡抑制蛋白(IAP)家族的最新成员〔1〕,是Altieri等(1997)利用效应细胞蛋白酶受体-1(effector cell protease re-ceptor 1,EPR1)cDNA在人类基因组库
目的 探讨足月新生儿脑梗死的高危因素及临床特征、预后,总结干预治疗措施.方法 2007年4月-2008年9月本科收治的足月新生儿脑梗死5例,占同期住院患儿的0.163%;男3例,女2例.均
目的 评价磁敏感加权成像在脑星形细胞瘤分级中的价值.方法 经病理证实的22例脑星形细胞瘤患者,按世界卫生组织2000年规定的胶质瘤分级标准分为2组,高级别组(Ⅲ～Ⅳ级)l3例,低
目的:分析纯钛表面微弧氧化改性对表面氧化膜特性的影响.方法:通过微弧氧化技术在含一定钙磷比例的电解液中制备纯钛表面氧化膜层,进而检测纯钛表面微弧氧化膜的粗糙度和接触
声检查准确率均为100%,A组在超声引导下进行颈内静脉穿刺的一次进针成功率、总成功率明显高于B组(P＜0.05),而并发症发生率、穿刺所用时间明显少于B组(P＜0.05).结论 急诊科医生
目的 探讨能有效提高行桡动脉穿刺采集血气分析标本患者舒适程度的护理模式. 方法将2007年7月-2008年6月住院行桡动脉穿刺采集血气分析标本的患者100例,按时间顺序随机分为对
为了更好地保护和利用好"天祝白牦牛"这一独特品种,完成优秀基因的保存,本项工作对冻精进行了制做,生产合格冻精5987剂,取得了满意的效果.