【摘 要】
：
The tribological behaviors were investigated in a new high strength and wear resistant aluminum bronze, with its friction coefficient and wear-rate lower than t
【机 构】
：
State Key Lab of Gansu New Non-ferrous Metal Materials,College of Mechanic-Electronic Engineering
【基金项目】
：
committee of Gansu science and technology of China
论文部分内容阅读
The tribological behaviors were investigated in a new high strength and wear resistant aluminum bronze, with its friction coefficient and wear-rate lower than those of ZQAl9-4 and ZQAl10-4-4 alloys in terms of Chinese national standard.The results showed that different tribological behaviors were attributed material itself. Under boundary lubrication condition, major wear mechanisms of aluminum bronze are adhesive wear and attrition wear. Its wearability depends mainly on material microstructure, shedding hard-particles, rakes and small pits that can store lubricant. The new aluminum bronze may find wide application in high sliding speed, heavy load and boundary lubrication condition.
其他文献
分析了农田水利的特点,阐述了农田水利基本建设的战略地位,并提出加强农田水利基本建设的措施,为农田水利建设的发展提供参考.
通过文献资料法和逻辑分析法,本文分析了当前哈尔滨市普通高校公共体育武术课教学中存在的不利因素,提出了在建构主义学习理论的基础上,尝试改变教学模式和教学方法,提高教学
提出了一种结合权值背景融合的小波域多尺度图像分割方法。首先通过小波域隐马尔可夫树模型获得图像各个尺度上的初始分割,然后为各个尺度上每一分割像素点分别赋予权值,并建立一种融合父子尺度信息的新背景模型,最后利用权值背景融合各个尺度图像初始分割结果,得到像素级分割。仿真结果表明,该方法可得到优于已有文献的分割效果。
电力系统全停或大面积停电后的黑启动策略的研究,是保证整个互联电网安全运行的重要课题.文中综述了黑启动的过程和恢复中存在的问题及相应的解决措施;指出建立自适应的黑启
A series of cubic SiC single crystals were heteroepitaxially grown by the hot-wall chemical vapor deposition (CVD) using a HMDS-C3H8-H2 system on 2 inch silicon
分别以相同面积的光滑 Pt电极和吸附了 Sm3+ 的铂电极作为工作电极 ,在酸性介质中采用循环伏安法对甲醇氧化进行测定 .结果表明 ,吸附了 Sm3+ 的 Pt电极上产生了更大的氧化电
本文报道了微重力条件下90°弯管内气液两相流型实验结果.弯管内径12.7 mm,弯曲半径76.5 mm,气、液两相表观流速分别为1.0～23.6 m/s和0.09～0.5 m/s.本文分析了观测到的弹状流、
In this paper, the study group has researched the comprehensive performance and application of the content of sulfur properly. Based on the research such a conc
The isochronal γ→α transformation of Fe-1Si alloy was measured by high-resolution dilatometry. According to the variation of the ferrite formation rate, an a
Micro-properties of the oxide scale and near-surface zone of a type 316 steel annealed in air and vacuum have been systematically investigated. Microstmctures o