论文部分内容阅读
Transformation-induced plasticity-aided steel was rolled at room temperature to different thickness reductions (0, 4%, 10%, 20%, 40%, and 60%). The mechanical properties, microstructure and austenite fractions of the rolled samples were measured by tensil