日本日兴株式会社研制的无机渗透性改性材料——混凝土增强玻璃,是在常温下形成的一种增强材料。它可分成两类:完全渗透型和渗透涂层型。前者渗透到混凝土内部,进行离子交换,使混凝土内部空隙形成陶瓷玻璃(人造石)。使混凝土从“石、砂、水泥”的硬化体转变成“石、砂和人造石”的硬化体;后者在混凝土表面也能形成玻璃涂层,此时有一部分渗透到混凝土内部,与混凝土形成一体化。 1.完全渗透型(离子置换型) 该类型是用硅酸钾为主要成分的水溶液,渗透
The inorganic permeability modified material developed by Japan Nikko Co., Ltd., a reinforced concrete glass, is a reinforcing material formed at room temperature. It can be divided into two categories: completely penetrating and penetrating coating types. The former penetrates into the interior of the concrete and undergoes ion exchange to form a ceramic glass (artificial stone) in the voids inside the concrete. The concrete is transformed from a hardened body of “stone, sand, cement” to a hardened body of “stone, sand, and artificial stone”; the latter can also form a glass coating on the surface of the concrete. At this time, part of the concrete penetrates into the concrete and the concrete. Form an integration. 1. Complete penetration type (ion replacement type) This type is an aqueous solution using potassium silicate as a main ingredient, penetrated