In order to further reduce the cost of AB5 type rare earth-based hydrogen storage alloy, a low-Co AB5 type hydrogen storage alloy were by substituting Co with C
【机 构】
：
Inner Mongolia Rare Earth Ovonic Metal Hydride Co.
论文部分内容阅读
In order to further reduce the cost of AB5 type rare earth-based hydrogen storage alloy, a low-Co AB5 type hydrogen storage alloy were by substituting Co with Cu and Fe.The characteristics of these alloys have been investigated by means of XRD, PCT, and measurement of electrochemical capacity and cycle life.The test results show that the effect of these two kinds of substituting elements on discharge capacity is Cu ＞ Fe, and the cycle life is on the contrary.Both of them have no distinct influence on activity speed, but activity speed increases with the decrease of Co.By the order way, the high discharge rate characteristics rise with the addition of Cu and decreasing of Co.
其他文献
Room temperature deformation behavior of A1-8Fe-2Mo-2V-1Zr alloy produced by spray forming and subsequent warm-extrusion at 693 K and/or rolling at 423 K was in
Irradiation-induced impurity segregation to grain boundaries is one of the important radiation effects on materials.For this reason, phosphorus segregation to p
The tensile fracture location characterizations of the friction stir welded joints of the AA1050-H24 and AA6061-T6Al alloys were evaluated in this study. The ex
LiFePO4 cathode material was synthesized by a solid-state reaction using doping several elements (Nb5 + ,Zr4 + ). The starting materials were mixed with a high-
Closed-cell type barrier ribs such as meander, honeycomb, SDR, and waffle types were produced using capillary molding process. Sintering of the ribs revealed th
The multi-arc ion plating technology was employed to prepare the molybdenum films with thickness of 3 μm on the AISI 1045 steel. The wear and scuffing tests we
The paper reviewed different explanations to the mechanism of glass polishing, the practices of glass polishing and the preparation of polishing powders, addres
研究了不同浓度苯丙胺在不同条件下对铜绿微囊藻的生长及毒性效应.结果表明,低浓度苯丙胺在弱碱性条件下促进铜绿微囊藻的生长;高浓度的苯丙胺则抑制其生长.苯丙胺对铜绿微囊
A Ml (NiCoMnA1)5 hydrogen storage alloys was prepared by double-roller rapid quenching.Its microstructure, electrochemically and kinetic characteristic were stu