An Al/Pb-0.3%Ag alloy composite anode was produced via composite casting.Its electrocatalytic activity for the oxygen evolution reaction and corrosion resistance was evaluated by anodic polarization curves and accelerated corrosion test,respectively.The microscopic morphologies of the anode section and anodic oxidation layer during accelerated corrosion test were obtained by scanning electron microscopy.It is found that the composite anode(hard anodizing)displays a more compact interfacial combination and a better adhesive strength than plating tin.Compared with industrial Pb-0.3%Ag anodes,the oxygen evolution overpotentials of Al/Pb-0.3%Ag alloy(hard anodizing)and Al/Pb-0.3%Ag alloy(plating tin)at 500 A·m–2were lower by 57 and 14 mV,respectively.Furthermore,the corrosion rates of Pb-0.3%Ag alloy,Al/Pb-0.3%Ag alloy(hard anodizing),and Al/Pb-0.3%Ag alloy(plating tin)were 13.977,9.487,and 11.824 g·m–2·h–1,respectively,in accelerated corrosion test for 8 h at 2000 A·m–2.The anodic oxidation layer of Al/Pb-0.3%Ag alloy(hard anodizing)is more compact than Pb-0.3%Ag alloy and Al/Pb-0.3%Ag alloy(plating tin)after the test.
An Al / Pb-0.3% Ag alloy composite anode was produced via composite casting. Iz electrocatalytic activity for the oxygen evolution reaction and corrosion resistance was evaluated by anodic polarization curves and accelerated corrosion test, respectively. Microscopic morphologies of the anode section and anodic oxidation layer during accelerated corrosion test were obtained by scanning electron microscopy. It is found that the composite anode (hard anodizing) displays a more compact interfacial combination and a better adhesive strength than plating tin. Compared with industrial Pb-0.3% Ag anodes, the oxygen evolution overpotentials of Al / Pb-0.3% Ag alloy (hard anodizing) and Al / Pb-0.3% Ag alloy (plating tin) at 500 A · m- 2were lower by 57 and 14 mV, respectively. of Pb-0.3% Ag alloy, Al / Pb-0.3% Ag alloy (hard anodizing), and Al / Pb- 0.3% Ag alloy were 13.977, 9.487, and 11.824 g · m -2 · h -1 , respectively, in accelerated corrosion test for 8 h at 2000 A · m-2.The an The oxidation rate of Al / Pb-0.3% Ag alloy (hard anodizing) was more compact than that of Pb-0.3% Ag alloy and Al / Pb-0.3% Ag alloy (plating tin)