采用CO2激光器对2 mm厚的AZ61镁合金细晶板材分别进行了填充焊和自熔焊实验.研究了细晶镁合金板材的焊接性和填充带合金化稀土元素Ce对接头组织及力学性能的影响.结果表明,细
【基金项目】
：
国家自然科学基金资助项目（51274092）
论文部分内容阅读
采用CO2激光器对2 mm厚的AZ61镁合金细晶板材分别进行了填充焊和自熔焊实验.研究了细晶镁合金板材的焊接性和填充带合金化稀土元素Ce对接头组织及力学性能的影响.结果表明,细晶板材的焊接接头热影响区不明显,组织较母材变化不大,半熔化区范围窄、液化程度低,未进行合金化的自熔焊焊缝组织较粗大,焊缝晶粒尺寸约15 μm,而填充焊焊缝组织为平均晶粒尺寸是5μm的等轴晶,即合金化稀土元素Ce可细化焊缝组织,而且稀土元素Ce的加入能抑制柱状树枝晶区而扩大等轴晶区域范围.填带焊接头的平均抗拉强度和伸长率较自熔焊接头分
其他文献
The paper describes the process of producing high quality magnesite-chrome bricks for VOD re-fining furnace,The service life reaches 14 heats,average life 12 he
The development and application of gunning mixes based on various material systems for repairing BOF,EAF,ladel and BF trough linings,using Chinese abundant natu
On the basis of determination of property and microstructure of two kinds of primary MgO-Cr2O3 bricks and residual magnesite-chrome bricks for super H-T tunnel
A tabular corundum(TC) with α-Al2O3 as main crystalline phazse has been made by elec-tro-fusion method,Its physical and chemical properties are: Al2O3 99.11%
AtWNK9为拟南芥WNK（With no lysine kinase）激酶家族成员,其功能尚不清楚.采用生物信息学和生物学实验相结合的方法,对AtWNK9蛋白结构、亚细胞定位、启动子元件、基因表达模式
针对几何非线性问题，基于S—R和分解定理与更新拖带坐标描述法，从运动变换的角度出发，由虚功率原理建立全局弱式积分方程．采用无网格Galerkin法（EFG）求得该问题的数值解．对于非线性