【摘 要】
:
在机电设备用Mg-Al-Zn系镁合金中添加了不同含量的合金化元素Sr或Ti,并进行了拉伸性能、耐磨损性能和抗疲劳性能的测试与分析。结果表明,添加适量的合金化元素Sr或Ti,尤其是
【机 构】
:
包头轻工职业技术学院能源工程学院,包头轻工职业技术学院汽车与机电工程学院,
论文部分内容阅读
在机电设备用Mg-Al-Zn系镁合金中添加了不同含量的合金化元素Sr或Ti,并进行了拉伸性能、耐磨损性能和抗疲劳性能的测试与分析。结果表明,添加适量的合金化元素Sr或Ti,尤其是复合添加Sr和Ti,可以提高Mg-Al-Zn系镁合金的拉伸性能、耐磨损性能和抗疲劳性能。与未添加合金元素相比,复合添加合金元素Sr和Ti可使其室温抗拉强度增加75 MPa、0℃抗拉强度增加95 MPa、室温磨损体积减少72.41%。
Different contents of alloying elements Sr or Ti were added into the Mg-Al-Zn magnesium alloy for mechanical and electrical equipment, and the tensile properties, wear resistance and fatigue resistance were tested and analyzed. The results show that adding appropriate amount of alloying element Sr or Ti, especially adding Sr and Ti, can improve tensile property, wear resistance and fatigue resistance of Mg-Al-Zn magnesium alloy. The addition of alloying elements Sr and Ti can increase the tensile strength at room temperature by 75 MPa, increase the tensile strength at 0 ° C by 95 MPa, and decrease the wear volume by 72.41% at room temperature.
其他文献
目的:讨论临床护理路径干预对小儿输液护理效果及护理满意度的影响.方法:研究时间:2019年4月-2019年12月.观察对象:在本院收治的150例接受输液治疗的患儿,以随机法将其分为对
目的:研究PDCA循环管理模式对新生儿红臀的预防效果.方法:病例样本为2019年2月-2020年2月时间段我院收治的64例新生儿,分组方式为随机数字表法,平均划分为2组,即研究组和对照
目的:评定助产责任制护理加产时体位管理用在产妇中对其分娩结局形成的影响价值.方法:选取2018年08月-2019年11月我院纳入的327例产妇,都怀有单胎,采用随机数字表方法分为参
目的:探究心理护理和健康护理对真菌性阴道炎患者的护理效果.方法:本次研究起止时间分别设定为2018年6月与2019年6月,将70名真菌性阴道炎患者纳入观察对象,按照1:1比例将70名
目的:分析新生儿护理中疼痛护理干预应用.方法:选取从2019年6月到2020年1月的新生儿,共200例,通过随机方法分成对照组与实验组,对照组对新生儿不采用任何缓释疼痛的治疗与干
目的:探讨护理干预对宫腔镜手术患者心理状态及疼痛的影响效果.方法:采集来自本院2018年7月至2019年11月阶段的116例宫腔镜手术患者,随机对分为58例,对照组运用常规护理,观察
目的:观察分析妇产科术后腹胀患者中医护理干预效果.方法:选取本院(在2019年1月-2019年7月)收治的122例妇产科术后腹胀患者,按照数字随机表法分为对照组(应用常规护理干预方
目的:讨论产房舒适护理对助产质量和产房内感染率的积极作用.方法:选取从2016年4月到2018年4月本院收治的孕产妇,共120例,对照组采取常规的护理方式,而实验组在采取产房舒适
目的:分析对前置胎盘者早期系统化护理中,行期待疗法对临床价值.方法:在本院采取随机的方式选出88名患有前置胎盘的产妇(2017年1月至2019年12月),随机分两组,一组为44名产妇,
目的:研究护理干预应用到妊娠期高血压患者中的护理作用与效果.方法:由2018年8月直到2019年7月,择选出我院收入的90例妊娠期高血压病例,依据方法的不同,可以分为观察组(n=45)