Increases of emission intensities for Eu3+ at the S6 site relative to that at the C2 site were observed as UV excitation wavelength decreases from 300 nm to 200 nm in both bulk and nanocrystalline cubic Y2O3:Eu3+. Decomposition of excitation spectra shows