以双酚S单体、ECH(环氧氯丙烷)为原料,在碱性条件下制得双酚S型EP(环氧树脂);然后以双酚S型EP/双酚A型EP作为复合EP,采用柔性固化剂制得复合EP胶粘剂。研究结果表明:当固化剂为D230时,复合EP胶粘剂的剪切强度相对最大;以复合EP胶粘剂胶接不同基材,则相应胶接件的剪切强度随双酚S型EP或D230含量增加均呈先升后降态势,并且在w(D230)=40%、w(双酚S型EP)=30%(相对于总树脂质量而言)时相对最大。 Bisphenol S type EP (epoxy resin) is prepared under the basic conditions with bisphenol S monomer and ECH (epichlorohydrin) as raw materials; then, bisphenol S type EP / bisphenol A type EP is used as a composite EP, the use of flexible curing agent composite EP adhesive. The results show that when the curing agent is D230, the shear strength of the composite EP adhesive is relatively the largest. When the composite EP adhesive is used to bond different substrates, the shear strength of the corresponding adhesive increases with the content of bisphenol S type EP or D230 Both increased first and then decreased and were relatively largest at w (D230) = 40%, w (bisphenol S type EP) = 30% (relative to the total resin mass).