【摘 要】
：
以醋酸锰、硝酸锂为原料,采用乙二胺四乙酸-柠檬酸(EDTA-CA)络合法,制备了正尖晶石型LiMn_2O_4超细粉末晶体.应用TG-DSC,XRD,CV及恒流充放电测试等手段对前躯体及LiMn_2O_4粉
【机 构】
：
华南理工大学化学与化工学院,广州,510641
论文部分内容阅读
以醋酸锰、硝酸锂为原料,采用乙二胺四乙酸-柠檬酸(EDTA-CA)络合法,制备了正尖晶石型LiMn_2O_4超细粉末晶体.应用TG-DSC,XRD,CV及恒流充放电测试等手段对前躯体及LiMn_2O_4粉体进行性能表征,确定了其最终的合成温度为600℃.常温下,组装成半电池,初始放电容量为120.2mAh/g,循环50次后容量保持在70%左右.“,”The super-fine powders of spinel LiMn_2O_4 were synthesized using EDTA-citric acid(EDTA-CA)by solgel method with manganese acetate,lithium nitrate as raw materials.The precursor and synthesized powders of LiMn_2O_4 were characterized by TG-DSC,XRD,CV and galvanostatic charge and diseharge.It is found that the optimal sintering temperature was 600℃.At room temperature,the initial discharge capacity of the half cell was 120.2mAh/g,and the capacity can also remain 70%of inithl capacity after 50 cycles.
其他文献
NEW HONS（江苏新宏基纺织科技有限公司）坐落于经济发达的张家港市，占地面积5万多平方米。公司长期专注于中高档毛纺面料研发和销售，是一家集研发、生产、销售和自营进出口权为一
在450K,pH值为11的条件下,以SbCl3,和Na2TeO3粉体为原料,用水热法制备了Sb2Te3纳米线。X-射线衍射(XRD)分析表明,所制的的材料为Sb2Te3,透射电镜(TEM)观察到Sb2Te3纳米线直径
2007年4月本院引入的高频电刀兼有电凝电切及氩离子凝固束的功能，内镜科主要将其应用于消化道息肉与出血的治疗中，现将电凝电切术与氩离子凝固术（Argon plasma coagulation，APC）在
以PVC糊树脂为基料,以柠檬酸酯(ATBC)、对苯二甲酸二辛酯(DOTP)、钙-锌稳定剂为原料,制备了四旋盖用密封胶,并研究该密封胶的加工性能及卫生性能.结果表明,该密封胶的加工性
目的 后路短节段钉棒系统治疗胸腰椎爆裂骨折临床疗效初步总结与分析.方法 对37例胸腰椎爆裂骨折行手术治疗并随访观察.结果 37例患者均获随访6～24个月,平均16个月,椎体占位比
目的探讨AF系统固定治疗胸腰段骨折的疗效。方法选择24例胸腰段骨折患者经切开复位，AF椎弓根系统内固定治疗。结果24例患者得到随访，都有一定程度的神经功能恢复和椎体高度恢复
以2,2,2-三氟乙醇钠,2,2,3,3,4,4,5,5-八氟戊醇钠和4-甲醛基苯酚钠为亲核试剂与聚二氯磷腈进行取代反应,后经硼氢化钠将醛基还原,得到了一种含有羟基的氟代烷氧基取代聚磷腈.
肿瘤的转移情况与肿瘤患者的疾病分期、治疗及预后密切相关。现就胃肠道肿瘤微转移灶的检测及意义作一综述。
在区域环境地质调查的基础上,从区域地质构造格局和活动性研究入手,分析了影响黄河下游悬河稳定的各种地质因素对悬河稳定性的控制作用,结果表明:济源-开封凹陷和东明断陷是