【摘 要】
：
研究了聚酰亚胺(PI)先驱体和发泡温度等工艺参数对PI泡沫结构的影响,采用DSC,TGA和光学显微镜对PI泡沫结构进行观察及表征。研究发现:先驱体的发泡温度应在150℃左右,随着发
【机 构】
：
南京工业大学学报编辑部,南京工业大学化学化工学院 南京210009,南京210009
论文部分内容阅读
研究了聚酰亚胺(PI)先驱体和发泡温度等工艺参数对PI泡沫结构的影响,采用DSC,TGA和光学显微镜对PI泡沫结构进行观察及表征。研究发现:先驱体的发泡温度应在150℃左右,随着发泡温度的升高,泡沫的密度降低;泡沫具有突出的开孔特性,开孔率高达93%以上;泡沫的密度主要取决于泡沫孔数和泡孔壁厚。
The effects of process parameters such as polyimide precursor and foaming temperature on the foam structure of PI were studied. The structure of PI foam was observed and characterized by DSC, TGA and optical microscope. The results show that the foaming temperature of the precursor should be about 150 ℃, the density of the foam decreases with the increase of the foaming temperature. The foam has the characteristic of open pores and the opening ratio is as high as 93%. The density of the foam depends mainly The number of foam holes and cell wall thickness.
其他文献
目的 探讨癌基因蛋白在垂体腺瘤发生过程中的作用及表达。方法 对 30例垂体腺瘤进行了 c- erb B-2、c- myc、bcl- 2及 P2 14种癌基因表达蛋白的免疫组织化学检测 ,并与其功
目的对CO2激光牙龈成形术与传统牙龈成形术方法的效果及优缺点进行比较.方法选择临床上牙龈肥大、增生患者42例,随机分成2组,一组行激光龈成形术,另一组采用手术龈成形术.结
目的观察女性冠心病的危险因素与冠状动脉造影特点,提高女性冠心病的诊断率.方法对61例疑诊为冠心病的女性行冠状动脉造影后分两组,冠心病组30例,冠状动脉狭窄*50%;非冠心病
目的本实验模拟临床前牙采用制成一定角度铸造桩核的方法,以改善前牙排列情况.方法采用Ansys有限元分析软件对不同角度桩核在牙根内的应力分布情况进行分析.结果牙根内应力与
[目的 ] 预测三峡建坝后洞庭湖泥沙淤积变化对血吸虫病流行因素的影响。 [方法 ] 分区域洲滩抽样的前瞻性研究。 [结果 ] 洞庭湖泥沙约 80 %来自长江。入湖三口泥沙含量最
探讨左旋18甲基炔诺酮皮下埋植避孕剂(皮埋剂)对机体细胞免疫功能的影响.对应用皮埋剂妇女159例(观察组)及31名对照组妇女,采用改良的碱性磷酸酶抗碱性磷酸酶桥联酶标染色技
目的 探讨女性腺性膀胱炎患者的尿动力学表现及其临床特征、形态学表现等的特点.方法 女性腺性膀胱炎患者32例,病程2个月～10年.回顾分析其主要临床表现;应用膀胱尿道镜作形态
[目的 ] 探讨湖区血吸虫病中度流行不同化疗策略的效果和费用。 [方法 ] 采用整群抽样于 1997～1999年 ,选择洞庭湖沿岸一线疫情基本一致的 12个自然村进行观察 ,居民感染率
本文用自拟益气活血汤辨证加减,对46例心律失常患者进行观察治疗,收到良好效果.现报告如下:
目的：研究大肠腺癌中抑癌基因p16的表达情况。方法：用免疫组化LSAB法检测71例结肠癌和直肠癌存档标本中P16蛋白的表达。结果：36例（50．70％）标本呈P16阳性，阳性细胞往往比阴性细胞有更