Carbide Dissolution during Intercritical Austenitization in Bearing Steel

来源 :武汉理工大学学报(材料科学版)(英文版) | 被引量 : 0次 | 上传用户:tnngx123
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
In order to investigate the carbide dissolution mechanism of high carbon-chromium bearing steel during the intercritical austenitization, the database of TCFE7 of Thermo-calc and MOBFE of DICTRA software were used to calculate the elements diffusion kinetic and the evolution law of volume fraction of carbide. DIL805A dilatometer was used to simulate the intercritical heat treatment. The microstructure was observed by scanning electron microscopy(SEM), and the micro-hardness was tested. The experimental results indicate that the dissolution of carbide is composed of two stages:initial austenite growth governed by carbon diffusion which sharply moves up the micro-hardness of quenched martensite, and subsequent growth controlled by diffusion of Cr elements in M3C. The volume fraction of M3C decreases with the increasing holding time, and the metallographic analysis shows a great agreement with values calculated by software.
其他文献
To gain a better understanding of the anticancer effects of hydroxyapatite (HAP) nanoparticles in vivo and in vitro, the effects of the interaction of HAP nanoparticles with hepatoma cells were explored. HAP nanoparticles were prepared by homogeneous prec
This work demonstrated quantitatively that DSA (dansylamide) and apo CA (dezincified carbon anhydrase) interacted with each other in the presence of Zn2+ (zinc ion). Thefl uorescence emission of DSA in the presence of Zn2+ and the intensity offl uorescenc
Ti-6Al-4V (TC4) alloys were plasma carbonized at different temperatures (900, 950, and 1 000?) for duration of 3 h. Graphite rod was employed as carbon supplier to avoid the hydrogen brittleness which is ubiquitous in traditional gas carbonizing process.
In order to increase the content of rare-earth oxides in magneto-optical glass and improve the Verdet constant, the rare-earth doped ternary Ga2O3-B2O3-SiO2(GBS) system magneto-optical glasses were prepared by the melt quenching technique. The influence o
In order to investigate the high-temperature performances of the asphalt pavement hot-applied sealant, as well as to reduce failures of the sealant pullout, the softening point test and the flow test (two existing methods for evaluating high-temperature p
Bio-ceramsite technology is one of the most effective technologies in the pretreatment of drinking water. In this work, bio-ceramsite was fabricated byCitrobacter freundii (C. freundii) immobilization on the ceramsite. Thefi ndings of the current study su