In order to prolong the working time of calcined flint clay-bauxite castables during construction at high temperature,boric acid was added into the castables.The effect of boric acid on working time and curing cold crushing strength of the castables at 25 ℃ and 35 ℃were investigated.After 24 h curing in mould and another 24 h curing at 110 ℃ after demoulding,the specimens were heat treated at 1 000 ℃,1 300 ℃,and1 500 ℃ for 3 h,respectively.The permanent linear change,bulk density,modulus of rupture,and cold crushing strength were determined.The result shows that there is no need to add boric acid when calcined flint clay-bauxite ca.stables works at 25 ℃ ; when calcined flint clay-bauxite castables works at 35 ℃,boric acid can increase the working time of the castables,but decrease the curing cold crushing strength a little.Adding boric acid into calcined flint clay-bauxite castables doesn t worsen performance of the castablcs.