【摘 要】
：
Influences of polymer-based grinding aid (PGA) on the damage process of concrete exposed to sulfate attack under dry-wet cycles were investigated. The mass loss, dynamic modulus of elasticity (Erd), and S and Ca element contents of concrete specimens were
【机 构】
：
Department of Material Science and Engineering, Southeast University, Nanjing, 210009 China;Jiangsu
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Influences of polymer-based grinding aid (PGA) on the damage process of concrete exposed to sulfate attack under dry-wet cycles were investigated. The mass loss, dynamic modulus of elasticity (Erd), and S and Ca element contents of concrete specimens were measured. Scanning electron microscopy (SEM), mercury intrusion porosimetry(MIP), and X-ray diffractometry(XRD) were used to investigate the changing of microstructure of interior concrete. The results indicated that PGA was capable of reducing the mass loss and improving the sulfate attack resistance of concrete. X-ray fluorescence (XRF) analysis revealed that PGA delayed the transport process of sulfate ions and Ca ions. In addition, MIP analysis disclosed that the micropores of concrete with PGA increased in the fraction of 20-100 nm and decreased in the residues of 200 nm. Compared with the blank sample, concrete with PGA had more slender and well-organized hydration products, and no changes in hydration products ratio or type were observed.
其他文献
The objective of this study was to investigate the effect of a new combined micro/nano-scale implant surface feature on osteoblasts\' behaviors including cell morphology,adhesion,proliferation,differentiation,and mineralization in vitro.A new micro/nano
The inlfuence of pre-deformation and heat treatment on mechanical properties of as-extruded ZK60 alloy was investigated. The experimental results indicated that the solid solution, pre-cold rolling and artificial aging treatments remarkably improved the m
To understand the effects of spray parameters on the splashing, cast iron particles were plasma-sprayed onto polished surfaces of aluminum substrate to form single splats. Various plasma arc powers and spray distances were applied to adjust the morphology
Two kinds of porous silicon (PS) were synthesized by magnesiothermic reduction of rice husk silica (RHS) derived from the oxidization of rice husks (RHs). One was obtained from oxidization/reduction at 500℃ of the unleached RHs, the other was synthesized