The precipitation mechanism of Ni75Al7.5V17.5 alloy above the L12 instability line, between the L12 and D022 instability lines and below the D022 instability line are studied using microscopic phase-field kinetic equation. This paper is aimed at investigating the effect of temperature on precipitation mechanism and morphological evolution of the alloy. Our simulations demonstrate that the precipitation is a mixed mechanism of non-classical nucleation growth and spinodal decomposition above the L12 instability line. It needs certain thermal fluctuations for nucleation and the number of θ phases is small at this temperature. The precipitation mechanism of γphase is congruent ordering followed by spinodal decomposition, and θ phase is a mixed mechanism of non-classical nucleation growth and spinodal decomposition between the L12 and D022 instability lines. The mechanism below the D022 instability line is similar to that between the L12 and D022 instability lines. With the decrease of the temperature, ordering and phase separation becomes fast, the dimension of γphase becomes small, the shape transforms from equiaxed to block, the dimension of θ phase becomes large and the shape transforms from strip to circle.