以酸活化的凹凸棒石(palygorskite,Pa)为载体,采用化学键合的方法制备了3-氨丙基三乙氧基硅烷(3-aminopropyl-triethoxysilane,APTES)硅烷化凹凸棒石(PaAPTES)负载的Keggin型杂多酸钴盐催化剂(Co4H1PV2Mo10O40/PaAPTES),并用红外光谱分析、X射线衍射、比Brunauer–Emmett–Teller(BET)表面积测定等对催化剂进行了表征。进行了催化氧化甲苯制苯甲醛的反应实验。结果表明:在采用Co4H1PV2Mo10O40/PaAPTES进行的催化反应中,苯甲醛是主要的生成产物。当乙腈为溶剂,催化剂的用量为0.3 g,9.6 mL双氧水(H2O2在溶液中体积含量为50%),在90℃反应9 h,得到甲苯转化率为58%,苯甲醛的选择性达到75%。且催化剂便于从反应体系中分离。
3-aminopropyl-triethoxysilane (APTES) silanized palygorskite (PaAPTES) was prepared by chemical bonding using acid-activated palygorskite (Pa) (Co4H1PV2Mo10O40 / PaAPTES) was synthesized and characterized by FTIR, X-ray diffraction and Brunauer-Emmett-Teller (BET) surface area measurements. The reaction of catalytic oxidation of toluene to benzaldehyde was carried out. The results showed that benzaldehyde was the main product of the catalytic reaction using Co4H1PV2Mo10O40 / PaAPTES. When acetonitrile was used as solvent, the amount of catalyst was 0.3 g and 9.6 mL of H2O2 (50% H2O2 in solution). The reaction was carried out at 90 ℃ for 9 h, yielding a toluene conversion of 58% and a benzaldehyde selectivity of 75% . And the catalyst facilitates separation from the reaction system.