【摘 要】
：
Steady-state corrosion and wear behaviors of two Al-bronzes, Cu-14Al-X and QAl9-4, in 5.0% H2SO4 solution were investigated. It is found that wear loss of bronz
【机 构】
：
State Key Laboratory of Advanced Non-Ferrous Materials
论文部分内容阅读
Steady-state corrosion and wear behaviors of two Al-bronzes, Cu-14Al-X and QAl9-4, in 5.0% H2SO4 solution were investigated. It is found that wear loss of bronzes in 5.0% H2SO4 solution is lower than that in water or in air, namely, it exhibits negative synergy between corrosion and wear. Further analysis shows that corrosive solution plays an important role in cooling of specimen during the sliding wear to prevent the reduction of the surface hardness of specimen, induced by frictional heat. On the other hand, the bronzes suffer a de-alloying corrosion, and a noble copper subsurface and patina form on the specimen surface in corrosive solution, which has a passive function for further corrosion. The noble copper subsurface experiences strain hardening during the corrosion and wear, resulting in the increase of the surface hardness thus the increase in wear resistance.
其他文献
The corrosion behavior of BFe10-1-1 alloy with different rare earth (RE) contents in simulated flowing marine water was investi-gated by X-ray diffractometer an
During deep drawing process, the material parameters of blank have a significant effect on the quality of the drawn part and the determination of process parame
Isometric heat capacity cv and isobaric heat capacity cp of Pt with stable and metastable phases were calculated by using pure element systematic theory. These
Effect of ion nitriding modification on surface hardness, corrosion resistance and magnetostriction of (Tb0.3Dy0.7)Fe1.95 alloy was investigated. Results demons
Unusual intense infrared-to-ultraviolet upconversion luminescence was observed in YF3:Yb3+(20%)/Tm3+(1%) nanocrystals under 980 nm excitation. The intense ultra
In the present work, the microstructures of A356 feedstock cast via a pipe consisting of partial inclined and partial vertical sections were investigated. The e
Pyrochlore oxides of general compositions, A2Zr2O7, where A is a 3+ cation (La to Lu), are promising candidate materials for ap-plications as high temperature t
The effects of mineral processing wastewater on sulfide minerals were investigated by flotation, infrared spectrometry and electrochemistry test. The results sh
The flow and concentration fields in a new style tubular stirred reactor were simulated by simulating the fluids dynamics(CFD), in which FLUENT software was use
It iS known that the strength of alloys can be successfully improved by rapid solidification. The paper presents a process where Cu-Cr-Sn-Zn lead frame alloy is