【摘 要】
：
To carry out biaxial tensile test in sheet metal, the biaxial tensile testing system was established. True stress-true strain curves of three kinds of aluminum
【机 构】
：
School of Mechanical Engineering and Automation,State Key Laboratory of Plastic Forming Simulation a
论文部分内容阅读
To carry out biaxial tensile test in sheet metal, the biaxial tensile testing system was established. True stress-true strain curves of three kinds of aluminum alloy sheets for loading ratios of 4:1, 4:2, 4:3, 4:4, 3:4, 2:4 and 1:4 were obtained by conducting biaxial tensile test in the established testing systems. It shows that the loading path has a significant influence on the stress-strain curves and as the loading ratio increases from 4:1 to 4:4, the stress-strain curve becomes higher and n-value becomes larger.Experimental yield points for three aluminum alloy sheets from 0.2% to 2% plastic strain were determined based on the equivalent plastic work. And the geometry of the experimental yield loci were compared with the yield loci calculated from several existing yield criteria. The analytical result shows that the Barlat89 and Hosford yield criterion describe the general trends of the experimental yield loci of aluminum alloy sheets well, whereas the Mises yield criterion overestimates the yield stress in all the contours.
其他文献
The microwave magnetic properties of the ball milled FeCo panicles were investigated as func tions of ball milling time ( t ) using microwave electromagnetic pa
Nb-15W-18Si-xHf (x = 0, 5, 10 and 15, mole fraction, %) alloys were prepared by arc melting and then homogenized at1 750 ℃ for 50 h. The microstructure and mec
A finite element analysis was carried out on the development of residual stresses during the cooling process from the fabrication temperature in the SiCp reinfo
Impermeability of tunnel structural material after exposure to high temperature determines residual service life and security. The present study explores imperm
Eu3+ doped SiO2 nano-crystalline glasses were prepared by sol-gel method. The broad peak of XRD pattern indicates an amorphous SiO2 matrix. The affection of ann
Long lasting phosphorescence (LLP) was observed in Eu2+, Ce3+ co-doped strontium borate glasses prepared under the reducing atmosphere due to the emission of bo
Phase formation in ternary system of complex Sc, Na and Li phosphates was studied at 950 ℃ and synthesis of new phases of definite composition was carried out.
Er3+/Yb3+-codoped oxyfluoride crystallite glass was prepared with melting technique. The compositions and the melting temperature and the annealing temperature
Based on crystal plasticity theory and surface layer model, relation of flow stress to billet dimension and grain size was built,and rationality of derived rela
The structure defects such as stray grains during unidirectional solidification can severely reduce the performance of single crystal turbine blades. A dendrite