大高径比H68铜套的多道次深拉深工艺与模具设计

来源 :热加工工艺 | 被引量 : 0次 | 上传用户:wangye31415926
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
结合经验设计与数值模拟,对大高径比H68铜套的多道次深拉深工艺与模具进行了设计,重点分析了材料、工艺以及模具对拉深过程的影响。发现H68铜套多道次拉深中会出现严重硬化;同时,压边圈与凸模间隙对成形过程有很大影响。根据理论分析结果,制定了优化的工艺与模具,得到了合格的零件。 Combined with experience design and numerical simulation, multi-pass deep drawing process and mold design of H68 copper sleeve with large height-diameter ratio were designed. The influence of material, process and mold on the drawing process were analyzed emphatically. It is found that H68 copper sleeve will have severe hardening in multi-pass deep drawing. Meanwhile, the clearance between blank holder and punch has a great influence on the forming process. According to the results of theoretical analysis, we developed the optimized process and mold, and got the qualified parts.
其他文献
通过实验研究了AlSi1铸锭反偏析现象。采用真空感应炉熔炼、石墨模铸造获得高纯AlSi1合金铸锭。利用电感耦合等离子体发射光谱仪分析铸锭中Si成分分布,采用间隙气体分析法分
Fluent软件是流体力学中通用性较强的一种商业CFD软件,应用范围很广.对它的程序结构、求解问题范围以及解决的步骤进行了介绍,讨论了在铸造过程中的具体应用.
采用传统的设计方法对中座零件的铸造工艺进行了设计。为了验证该工艺的合理性,采用最新的铸造模拟软件对所设计的铸造工艺进行了模拟验证。模拟结果表明,采用传统方法设计的
基于自适应网格技术模拟了金属棒10CrMoV的连续铸造过程。考虑铸造过程中相变的发生及随温度变化的热物理属性,根据浇铸速率和冷却速度,对金属棒连续铸造过程进行热和流体动
为了研究含氟渣系成分变化对熔化温度的影响,根据五因素二次正交旋转回归法设计渣系配方,使用CQKJ-Ⅱ型高温矿渣熔化温度特性测定仪,采用半球法对CaF2-SiO2-Al2O3-CaO-MgO渣
针对某铸造铝铜合金铸件薄壁复杂结构特点和铸造合金特性,研究了其铸造工艺.借助数值模拟技术预测缩孔、缩松缺陷,并通过热处理后合金力学性能测试,优化铸造工艺,试制出了合
通过对AZ91D镁合金壳体件液态模锻实验,研究了挤压压力对其组织与性能的影响.结果表明,液态模锻零件的组织由α-Mg+β3-Mg17Al12组成,在压力作用下α相枝晶被细化,形态改善,
利用有限元软件,对CSP轧后层流冷却过程进行了温度场模拟。对比了层流冷却的3种不同冷却方式,即前段连续冷却、前段间断冷却和后段连续冷却。分析了带钢的温度场,确定了快速
在高强度钢板热冲压成形中,高温下材料软化,如果压料设计的不合理,导致压边力分布不均匀,板料在成形时极易形成皱褶、叠料与破裂等成形问题.因此,确定合理的热冲压成形压料方
摆辗塑性铰是摆辗过程中产生的非稳态因素之一,在材料成形中要避免是困难的,但到目前为止,对其成形机理研究很少。对圆环件进行了建模,采用DEFORM-3D软件对摆辗过程进行了模