The effects of heat treatment on the dynamic compressive properties and energy absorption characteristics of open cell aluminum alloy foams (Al-Mg-Si alloy foam and Al-Cu-Mg alloy foam) produced by infiltrating process were studied. Two kinds of heat treatment were exploited: age-hardening and solution heat treating plus age-hardening (T6). The split Hopkinson pressure bar (SHPB) was used for high strain rate compression test. The results show that both age-hardened and T6-strengthened foams exhibit improved compression strength and shortened plateau region compared with that of foams in as-fabricated state under high strain rate compression, and the energy absorption capacity is also influenced significantly by heat treatment. It is worthy to note that omitting the solution treating can also improve the strength and energy absorbed much. The effects of heat treatment on the dynamic compressive properties and energy absorption characteristics of open cell aluminum alloy foams (produced by infiltrating process were studied. Two kinds of heat treatment were exploited: age-hardening and solution heat treating plus age-hardening (T6). The split Hopkinson pressure bar (SHPB) was used for high strain rate compression test. The results show that both age-hardened and T6-enhanced foams exhibit improved compression strength and shortened plateau region compared with that of foams in as-fabricated state under high strain rate compression, and the energy absorption capacity is also indicated significantly by heat treatment. It is worthy to note that omitting the solution treating can also improve the strength and energy pumping much.