【摘 要】
：
采用一步法对钢铁表面化学吸附成膜技术进行了研究,通过单因素试验优化出较佳的工艺条件:聚乙二醇(400)20mL/L,三乙醇胺40mL/L,硅烷偶联剂10mL/L,丙三醇15mL/L,温度45°C,pH=
【机 构】
：
廊坊师范学院化学与材料科学学院,河北大学化学与环境科学学院,
论文部分内容阅读
采用一步法对钢铁表面化学吸附成膜技术进行了研究,通过单因素试验优化出较佳的工艺条件:聚乙二醇(400)20mL/L,三乙醇胺40mL/L,硅烷偶联剂10mL/L,丙三醇15mL/L,温度45°C,pH=10,处理时间8min。试验结果表明,在此条件下得到的化学吸附膜耐硫酸铜点滴时间为68s,附着力0级,冲击强度50kg·cm。该化学吸附膜综合性能优于传统的磷化膜。
A one-step method was used to study the film-forming technology of chemical adsorption on the surface of steel. The optimum technological conditions were optimized by single factor experiment: polyethylene glycol (400) 20mL / L, triethanolamine 40mL / L, silane coupling agent 10mL / L, glycerol 15mL / L, temperature 45 ° C, pH = 10, the processing time 8min. The experimental results show that the chemical adsorption film obtained in this condition is resistant to the dripping time of copper sulfate at 68s, the adhesion of 0, the impact strength of 50kg · cm. The chemisorption film is superior to the traditional phosphate film.
其他文献
利用复变函数方法,通过构造广义保角映射,研究了一维正方准晶垂直于准周期方向具有不对称共线裂纹的圆形孔口问题,给出了各应力分量在象平面的复表示,并得到该裂纹尖端的应力
目的建立同时测定檀香叶中牡荆苷与异牡荆苷含量测定方法,为其资源利用等提供依据。方法采用Agilent TC-C18色谱柱(4.6 mm×250 mm,5μm),流动相为甲醇-0.5%冰醋酸溶液(40∶6
采用半经验的Gupta多体势结合分子动力学方法,系统的研究了Ni38、Pd38、Pt38团簇的熔化特性,我们发现这3种团簇的熔化行为均有别于热熔曲线呈现一宽峰的满壳层结构的团簇的熔
本文研究了一个二元广义Weibull分布模型,其边缘分布分别是一元广义Weibull分布.利用EM算法,得到了未知参数的极大似然估计和观测Fisher信息矩阵.
为探索红外光谱技术在辐射效应研究中的应用,以合肥同步辐射红外和远红外光谱实验站为平台开展软X射线低剂量辐射效应研究。用傅里叶变换红外显微镜光谱仪采集软X射线辐照前
回顾了由二元关系产生的粗糙近似空间及其导出的各种粗鞋近似算子的构造性定义，介绍了经典和模糊环境下各种信任结构及其导出的信任函数与似然函数的概念，给出了粗糙集理论
根据定位基团类型并结合其反应机理,介绍了近几年来钌催化的C-H键活化构建C-C键的研究进展.参考文献40篇.
应用涉及更远邻原子的改进分析型嵌入原子方法(MAEAM)计算了面心立方(fcc)金属(Ag,Al,Au,Cu,Ir,Ni,Pd,Pt,Rh)的空位性能.在MAEAM计算中,考虑了远邻原子相互作用和单空位迁移
在BnNH2.TFA/1,4-二氮杂二环[2.2.2]辛烷催化下,α-取代的苄叉丙酮与α-取代β-酮酸酯发生Mi-chael加成反应,合成了季碳-叔碳化合物——α,α-双取代β-酮酸酯,其结构经1H NM
针对铝锌热镀板存在的问题,通过添加合金元素的方式,提高了铝锌镀板的性能,为该类镀板使用领域的扩大和产品质量的改进提供了途径。
Aiming at the existing problems of al